SABIC Innovative Plastics LNP VERTON PX06418 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON PX06418 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 1.10 % | 1.10 % | 50% RH, 24 hrs; ASTM D570 |
| 1.70 % | 1.70 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 182 MPa | 26400 psi | 5 mm/min; ISO 527 |
| 203 MPa | 29400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 193 MPa | 28000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.9 GPa | 1580 ksi | 1 mm/min; ISO 527 |
| 11.96 GPa | 1735 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| 307 MPa | 44500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 309 MPa | 44800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.53 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.84 J/cm | 5.32 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.4 J/cm | 19.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 114 µm/m-°C @Temperature -30.0 - 30.0 °C |
63.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Materion moldMAX® HH High Hardness Beryllium Copper Alloy
- Industrial Laminates/Norplex NP504 Glass Fabric
- Gouda Vuurvast CURAS SiC 70 D GM Moldable Refractory Material
- Latrobe LSSâ„¢ A7 Mod. Wear-Resistant Tool Steel (ASTM A7 Mod.)
- MetalTek MTEK 29-17 Cast UNS J94003 Heat Resistant Stainless Steel
- Lubriplate NO.105 NO. 105 Motor Assembly Grease Specialty Lubricant and Grease
- Multibase C6-250 VAROX DBPH Dow-Corning Class VI Elastomer
- Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled
- BASF Elastollan R 2005/1 20% Glass Filled TPUR
- 3M Scotchcal™ 1000-46 Graphic Film
Copyright © lookpolymers.com All Rights Reserved