Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer Westlake Plastics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medical grade Radel R5500 resin offers exceptional hydrolytic stability, toughness, heat deflection temperature and resistance to stress cracking. This polymer also has excellent thermal stability, and impact strength over a wide temperature range. Recommended sterilization techniques for Radel R5500 include EtO gas, radiation, steam autoclaving, dry heat and cold sterilization.Radel® is a trade name of Solvay Advanced Polymers. Information provided by Westlake Plastics.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Water Absorption 0.37 %
0.37 %
ASTM D570; 24 hrs.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 69.6 MPa
10100 psi
ASTM D638
Elongation at Break 60 - 120 %
60 - 120 %
ASTM D638
Elongation at Yield 7.2 %
7.2 %
ASTM D638
Tensile Modulus 2.34 GPa
340 ksi
ASTM D638
Flexural Yield Strength 91.0 MPa
13200 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Compressive Yield Strength 98.94 MPa
14350 psi
ASTM D695
Compressive Modulus 1.73 GPa
251 ksi
ASTM D695
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Tensile Impact Strength 399 kJ/m²
190 ft-lb/in²
ASTM D1822
Thermal Properties Metric English Comments
CTE, linear 55.8 µm/m-°C

@Temperature 20.0 °C
31.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Thermal Conductivity 0.349 W/m-K
2.42 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 214 °C
417 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.787 mm
V-0

@Thickness 0.0310 in