Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 405 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D-648
PlastiComp Complet® LGF30 - PA6 Nylon 6, 30% Long Glass Fiber Reinforced
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 6 with 30% long glass fiber reinforcementInformation provided by PlastiComp, Inc..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
Nylene® Vexel™ B12GF30 SA , 30% Glass Reinforced PBT
Description: Vexel™ B12GF30 SA is a 30% glass fiber reinforced PBT with improved surface aPolyphenylene Etherarance. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
Oxford Polymers 10GF 10% Glass Fiber Filled Polyetherimide for Extrusion and Injection Molding
10% Glass Fiber Filled Polyetherimide for Extrusion and Injection MoldingInformation provided by Oxford Polymers.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM Data
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry)  (discontinued **)
Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
RTP Company RTP 2102 TFE 15  Polyetherimide (PEI) Glass Fiber 15% - PTFE 15%  (discontinued
Glass Fiber 15% - PTFE 15%Comments:Glass FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provide..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
Fiberfil® FPI-33 BK Nylon 6, 33% Glass Reinforced, post industrial
Information provided by FIBERFIL Engineered Plastics
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM CRS5001 PEI
Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 listing.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
Unannealed; ASTM D648
Solvay Specialty Polymers Radel® R-5000 Polyphenylsulfone (PPSU)
Radel® R-5000 is a transparent polyphenylsulfone (PPSU) which offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins...
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Radel® R-5100 Polyphenylsulfone (PPSU), Filled
Radel® R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, that offers exceptional hydrolytic stability, and toughness superior to other commercially-available, h..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® 420 PBT (Asia Pacific)
30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Stat-kon EE005 PEI
LNP STAT-KON* EE005 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the ..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Stat-kon EE006EM PEI (Asia Pacific)
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by ..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6 GF30 L X MT 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: LubricantFeatures: LubricatedAppearance: SilverTPCI# 7210102Information provid..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp EC002E PEI (Asia Pacific)
LNP THERMOCOMP* EC002E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP QF008 PA 6/10 (Asia Pacific)
LNP* Thermocomp* QF008 is a compound based on Nylon 6/10 resin containing Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
405 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp QF008S PA 6/10
LNP* Thermocomp* QF008S is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 6.40 mm
405 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM 2110R PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 1005 TFE 10 Polybutylene Terephthalate (PBT), Glass Fiber Reinforced - PTFE Lubricated
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 1400 AG-210 Polyethersulfone (PES), Glass Fiber - UL94 V-0
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 2183 HF Polyetherimide (PEI), Carbon Fiber
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 2101 Polyetherimide (PEI), Glass Fiber
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 2102 Polyetherimide (PEI), Glass Fiber
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D 648
RTP Company RTP 2107 LF Polyetherimide (PEI), Glass Fiber - Low Flow
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
3300HR PBT, 30% Glass Reinforced
Celanex 3300HR is a 30% glass reinforced polybutylene terephthalate which has excellent hydrolysis resistance, mechanical properties and processabilityInformation provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
Ashley Polymers Ashlene® 149WO PBT Polyester, 45% Glass Reinforced
A flame retardant PBT polyester with 45% glass reinforcement, mineral filled.Data provided by the manufacturer
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Annealed, 0.125 in bars; ASTM D648
PolyOne Edgetek® NI-20GF/000 Nylon 6/10, Glass Filled  (discontinued **)
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Unannealed; ASTM D648
LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ISO 75-1/-2
DuPont Performance Polymers Crastin® HR5330HF BK503 PBT  (Unverified Data**)
Crastin® HR5330HF is a 30% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resis..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ASTM D648
RTP Company RTP 282B TFE 15  Nylon 6/10 (PA 6/10) Carbon Fiber 15% - PTFE 15%  (discontinued
Carbon Fiber 15% - PTFE 15%Comments:Carbon FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provi..
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON PX06418 PA 6
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.