- Teijin Multilon DN-3510F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Teijin Multilon DN-3510F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon DN-3510F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 10 % filler. Improved stiffness and high fluidity realizes a thin wall of OA machines etc.Applications:Thin wall components of mechanical, electric and electronic equipment that need least warpage and dimensional accuracy etc.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm |
0.0050 - 0.0070 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 50mm/min; ISO 527 |
| Elongation at Break | 35 % | 35 % | 50mm/min; ISO 527 |
| Tensile Modulus | 3.90 GPa | 566 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ISO 75 |
| Vicat Softening Point | 105 °C | 221 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.00 mm |
V-1 @Thickness 0.0394 in |
|
| V-0 @Thickness 1.30 mm |
V-0 @Thickness 0.0512 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Termopol Termoton® V2GA0065A TPV Compound
- ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact (discontinued **)
- Ipiranga Petrochem PH 0141 Polypropylene
- STAR Thermoplastic Alloys & Rubbers StarXTRUDE XTR-80-1000 TPE
- DuPont™ Surlyn® 1605 Sodium Ionomer Resin for Blown/Cast Film and Extrusion Coating
- DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30
- Dymax 914-A Strain Relief, Wire and Parts Tacking Adhesive
- Colorite Polymers 3876 General Purpose Vinyl Compound
- Lubrizol ESTANE® 58311 Ether Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved