Styron EMERGEâ„¢ 7100 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 7100 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: EMERGEâ„¢ PC/ABS 7100 advanced resin exhibits a balance of properties between impact strength, heat resistance and processability. Its superior natural base color and lot-to-lot color consistency makes it ideally suited for producing very consistent colored parts. It has excellent flow and is ideal for injection molding in thin-wall applications, such portable electronic devices.Information provided by Styron
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 4.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 4.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
25 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 25 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112

@Thickness 3.20 mm
 112

@Thickness 0.126 in
 Injection Molded; ASTM D785
Tensile Strength, Yield 50.3 MPa

@Thickness 3.20 mm
 7300 psi

@Thickness 0.126 in
 50 mm/min, Injection Molded; ASTM D638
Elongation at Break 50 %

@Thickness 3.20 mm
 50 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Yield 4.0 %

@Thickness 3.20 mm
 4.0 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Modulus 2.10 GPa

@Thickness 3.20 mm
 305 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Flexural Strength 80.0 MPa

@Thickness 3.20 mm
 11600 psi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Flexural Modulus 2.34 GPa

@Thickness 3.20 mm
 339 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Izod Impact, Notched 2.90 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 5.43 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 Injection Molded; ASTM D256
4.80 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 8.99 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.0 µm/m-°C
42.2 µin/in-°F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 116 °C

@Thickness 3.20 mm
 241 °F

@Thickness 0.126 in
 Unannealed, Injection Molded; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C

@Thickness 3.20 mm
 203 °F

@Thickness 0.126 in
 Unannealed, Injection Molded; ASTM D648
Vicat Softening Point 133 °C

@Load 1.02 kg
 271 °F

@Load 2.25 lb
 Rate B (120°C/h); ASTM D1525
Flammability, UL94 HB

@Thickness 1.00 mm
 HB

@Thickness 0.0394 in
Processing Properties Metric English Comments
Melt Temperature 238 - 266 °C
460 - 511 °F
Mold Temperature 48.9 - 90.6 °C
120 - 195 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour