Solvay TECHNYL® A 60 G2 V30 PA66, 30% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 60 G2 V30 PA66, 30% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: High flow Polyamide PA66 Flame retarded grade reinforced with 30% glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This Red Phosphorous and Halogen free flame retardant grade, combines excellent all-round mechanical properties with outstanding flame retardancy. This product is ideally suited for large and small appliances and connectic applications requiring glow wire no flame performance. This product is registered at the VDE institute for the IEC 60335 normative in all color references down to 0.8mm thickness. It has a robust GWIT/GWT pass with excellent CTI (>550V) and ball pressure test performance (>150°C). This product is available in Natural, Grey and Black. Specific colors and Laser Marking grades optimized for YAG and UV laser types are also available upon request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183/A
Linear Mold Shrinkage, Flow 0.0123 cm/cm
0.0123 in/in
Linear Mold Shrinkage, Transverse 0.0056 cm/cm
0.0056 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
ISO 527 Type 1A
Elongation at Break 2.5 %
2.5 %
ISO 527 Type 1A
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527 Type 1A
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 256 °C
493 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 247 °C
477 °F
ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
1210
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
1210
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
1210
Glow Wire Test 800 °C

@Thickness 0.800 mm
1470 °F

@Thickness 0.0315 in
ignition temperature; ISO 60695-2-13
850 °C

@Thickness 1.60 mm
1560 °F

@Thickness 0.0630 in
ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
ISO 60695-2-12
960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
ISO 60695-2-12
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
ISO 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Front Barrel Temperature 260 - 270 °C
500 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 260-270°C