- Reltek BONDiT™ B-482 Adhesive, Sealant & Coating System
Reltek BONDiT™ B-482 Adhesive, Sealant & Coating System
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | Reltek LLC |
| Trade Name | BONDiT™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Reltek BONDiT™ B-482 Adhesive, Sealant & Coating System.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Properties: Excellent balance of chemical, electrical, and mechanical properties.Ruggedized, semi-flexible system.Very clean system.Ease of use.Applications: Encapsule sensitive instrumentation for chemical isolation, outstanding moisture resistance, ruggedness and flexibility. Suitable for clean room use and direct contact with semiconductors. Very easy to use and clean two-part system. Superior for coating in marine applications and other harsh environments. Tough, chemically-resistant, non-blush clear coating with medium gloss finish. Bonds to most substrates. Ambient 24 hour or accelerated thermal cure.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | <= 1.0 % | <= 1.0 % | 24hrs boiling DI water |
| Viscosity | 2500 cP | 2500 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 17.94 MPa | 2602 psi | 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Tensile Strength, Ultimate | 18.73 MPa | 2716 psi | Peak; 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Tensile Strength, Yield | 18.73 MPa | 2717 psi | 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Elongation at Break | 23.9 % | 23.9 % | 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Elongation at Yield | 11.3 % | 11.3 % | 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Tangent Modulus | 369.11 MPa | 53535 psi | 2hrs @200°F+45days @ ambient; 2:1 Volume mix |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 177 °C | 350 °F | |
| Minimum Service Temperature, Air | -45.6 °C | -50.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 360 min | 6.00 hour | Ambient Set |
| 720 min | 12.0 hour | Ambient, tack free | |
| 1440 min | 24.0 hour | Ambient, 95% cure | |
| 240 min @Temperature 65.6 °C |
4.00 hour @Temperature 150 °F |
98% cure | |
| Pot Life | 40 min | 40 min | Ambient |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical & Moisture Resistance | 2.5 | 0=Lowest, 4=Highest |
| Color | Clear with slight amber | |
| Flexibility Ranking | 3 | 0=Rigid, 5=Highly Flexible |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2280 Amorphous Polyalphaolefin (APAO)
- Novum Glass Solid Soda-lime Industrial Series Glass Microspheres
- PolyOne Geon™ Vinyl Flexible D7000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lehmann & Voss LUVOCOM® 1105-7794/BL PEEK, unreinforced
- Lucite International Diakon® CLG340 Acrylic Polymer
- Techmer ES HiFill® PA6/6 GF30 L 30% Glass Filled
- Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Homopolymer Polypropylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N990 (MT) Filler
- EMS-Griltech Griltex® D 1299A Heat Stabilized Copolyamide Hotmelt Adhesive (Technical Applications)
Copyright © lookpolymers.com All Rights Reserved