Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE  (discontinued **)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE  (discontinued **).pdf
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 5002 is a 20% glass-fiber reinforced, PTFE modified polyarylamide which exhibits very good mechanical performance, very good surface gloss, and superior wear properties.- Natural: Ixef 5002/0085- Custom ColorableFeatures: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Wear Resistance; High Flow; High Stiffness; High Strength; Low Friction; Low Moisture Absorption; Outstanding Surface FinishUses: Appliance Components; Appliances; Automotive Applications; Automotive Electronics; Bushings; Business Equipment; Cams; Cell Phones; Electrical Housing; Electrical/Electronic Applications; Furniture; Gears; Industrial Applications; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Power/Other ToolsAvailability: Africa & Middle East; Asia Pacific; Europe; North America; South AmericaHot Runners: 250°C to 260°C (482°F to 500°F)Injection Pressure: rapidDryingThe material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).Injection MoldingIXEF 5002 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 290°C (500°F to 554°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F).To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Information provide by Solvay Specialty Polymers
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Water Absorption 0.22 %
0.22 %
24 hrs; ISO 62
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
ISO 527-2
Elongation at Break 2.2 %
2.2 %
ISO 527-2
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527-2
Flexural Strength 215 MPa
31200 psi
ISO 178
Flexural Modulus 8.00 GPa
1160 ksi
ISO 178
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
Izod Impact, Unnotched 3.70 J/cm
6.93 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 29.0 µm/m-°C
16.1 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Unannealed; ISO 75-2/A
Oxygen Index 23 %
23 %
ISO 4598-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Dielectric Constant 3.9

@Frequency 110 Hz

@Frequency 110 Hz
IEC 60250
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 60243-1
Dissipation Factor 0.015

@Frequency 110 Hz

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Additional Properties Moisture Absorption - Internal Method: 1.8 %
Appearance Colors Available; Natural Color
Forms Pellets
Processing Method Injection Molding
RoHS Compliance RoHS Compliant