Polymer Property : Tensile Strength at Break = 19600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	135 MPa	19600 psi	STN EN ISO 527-2
Plastcom SLOVAMID 66 GF 25 FRI 3 Polyamide 66, 25% Glass Fiber, Halogen Free Flame Retardant FeaturesPA 66 for injection moulding, chemically reinforced with 25% glass fiber and non-halogen flame retardant, with heat and flammability resistance, achieves V-0 in accordance with UL 94. Non-h..
Tensile Strength at Break	135 MPa	19600 psi	50 mm/min; ASTM D638
Ovation Polymers RIGITRON 20433 GF PBT, 33% Glass Reinforced PBT - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco..
Tensile Strength at Break	135 MPa	19600 psi	ISO 527
Nilit FRIANYL B63 GV15 Nylon 6 for injection molding, 15% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	135 MPa	19600 psi	ISO 527-1/-2
DSM Akulon® S223-PG6U (Dry) 33% Glass Reinforced, Impact Modified Nylon 66 (North America) (discontinued **)& Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break	135 MPa	19600 psi	10mm/min; ASTM D638
Kingfa PBT-G30 30% Glass Fiber Reinforced PBT Features:Good size stabilityHigh mechanical propertiesHigh heat resistanceExcellent balance propertiesApplications:Injection moldingApplication partsAuto handleDoor latchE & E partsInformation Provi..
Tensile Strength at Break	135 MPa	19600 psi	ISO 527-1/-2
Lanxess DurethanÂ® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral PA 6, injection molding grade, 40% glass fibers/mineral, good heat-ageing resistance, good surface, good flowability (Easy Flow), low warpage
Tensile Strength at Break	135 MPa	19600 psi	ISO 527-1/-2
Lanxess DurethanÂ® DP AKV 30 FN00 000000 Nylon 66, 30% Glass Fiber PA 66, injection molding 30% glass fibers, UL 94 V-0 at 0.4 mm, max. temperature in glow wire test: 960 Â°C at 0,75 mm, free from halogen and red phosphorous
Tensile Strength at Break	135 MPa	19600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS com..
Tensile Strength at Break	135 MPa	19600 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP IF006L PA 6/12 (Asia Pacific) LNP* THERMOCOMP* IF006L is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength at Break	135 MPa	19600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON DEL359EF PC LNP* STAT-KON* DEL359EF is a compound based on Polycarbonate containing 25% Carbon Fiber, 15% PTFE. Added features include: Flame Retardant. Electrically Conductive, Wear Resistant.
Tensile Strength at Break	135 MPa	19600 psi	ASTM D638
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength at Break	135 MPa	19600 psi	ASTM D638
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength at Break	135 MPa	19600 psi	ASTM D638
A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength at Break	135 MPa	19600 psi	ISO 527-93
Wellman Wellamid® MRGF25/25 22H-NBK1 Nylon 66, 25% Mineral and 25% Glass Reinforced All information provided by Wellman Engineered Resins.
Tensile Strength at Break	135 MPa	19600 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 4107 black 9992 PA612-GF40 Product description: Grilamid XE 4107 black 9992 is a 40% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4107 are: low water absorpti..
Tensile Strength at Break	135 MPa	19600 psi	5 mm/min; ISO 527
Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding Staramide ACF2 is a 10% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	135 MPa	19600 psi	5 [mm/min]; ISO 527-2/5
Akro-Plastic Akromid® B3 GF 50 RM-M (3146) PA 6 Conditioned, 50% Glass Filled In all, the construction relevant features show that the significantly reduced moisture absorption of AKROMID B3 GF 30 RM leads to increasing rigidities and strengths as already expected. Neverthele..
Tensile Strength at Break	135 MPa @Temperature -40.0 °C	19600 psi @Temperature -40.0 °F	ASTM Test
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi..
Tensile Strength at Break	135 MPa @Temperature -40.0 °C	19600 psi @Temperature -40.0 °F	ISO Data
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi..
Tensile Strength at Break	135 MPa	19600 psi	ISO 527-2
Ascend Performance Materials Vydyne® R530H BK02 Nylon 66, 30% Glass Reinforced, Conditioned Vydyne® R530H BK02 is high-flow, 30% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when expose..
Tensile Strength at Break	135 MPa	19600 psi	ASTM D638
Beijing Chemical Industry KAIFA® HN201-G30 PA6 Resin 30% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	135 MPa	19600 psi	ISO 527 Type 1A
Solvay TECHNYL® A 216 V30 Natural FA PA66, 30% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 30% of glass fiber and modified for enhanced injection molding.Available in: Europe Product Applications: This material offers an excellent combination b..
Tensile Strength at Break	135 MPa	19600 psi
LATI Latiohm 75/4-03 PD01 G/20 PBT, 20% Glass Fiber Reinforced Semiconductive/dissipative product based on Polybutylene Terephthalate (PBT). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided..