Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA), 33% Glass Fiber.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® HFZ A-1133 L is a high-flow, 33% glass fiber reinforced polyphthalamide (PPA) grade.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Flow; High Stiffness; High Strength; High Temperature StrengthUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bobbins; Connectors; Electrical/Electronic Applications; General Purpose; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Mechanical Properties Metric English Comments
Tensile Strength at Break 188 MPa
27300 psi
ISO 527-2
Elongation at Break 1.7 %
1.7 %
ISO 527-2
Tensile Modulus 11.2 GPa
1620 ksi
ISO 527-2
Flexural Strength 268 MPa
38900 psi
ISO 178
Flexural Modulus 10.4 GPa
1510 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180
Charpy Impact, Notched 0.820 J/cm²
3.90 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 296 °C
565 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 316 - 329 °C
601 - 624 °F
Middle Barrel Temperature 316 - 329 °C
601 - 624 °F
Front Barrel Temperature 324 - 335 °C
615 - 635 °F
Melt Temperature 321 - 345 °C
610 - 653 °F
Mold Temperature 150 °C
302 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Suggested Max
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Latin America
North America
Color Black; Natural
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant