Tra-Con Tra-Duct 921M01 Low Viscosity Long Pot Life Silver-Filled Epoxy

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy, Electrically Conductive , Filled/Reinforced Thermoset
Manufacturer Tra-Con, Inc.
Trade Name Tra-Duct
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Duct 921M01 Low Viscosity Long Pot Life Silver-Filled Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-DUCT 921M01 is a two component, silver-filled electrically conductive epoxy adhesive designed for applications which require electrical conductivity and a long pot life at a relatively low heat cure. This adhesive is a soft, smooth paste ideal for application by automatic dispenser, screen-printing, or hand probe. This material can be conveniently packaged in our custom bipax as well as pre-mixed and frozen syringes. Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Specific Gravity 3.61 g/cc
3.61 g/cc
Cured
Viscosity 23000 cP
23000 cP
Mixed (cp #52, 10 rpm)
Mechanical Properties Metric English Comments
Adhesive Bond Strength 10.3 MPa
1500 psi
Lap shear, alum to alum
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 105 °C
221 °F
Ultimate Tg
Electrical Properties Metric English Comments
Volume Resistivity 0.00017 ohm-cm
0.00017 ohm-cm
cured 15 min @ 150°C
0.00025 ohm-cm
0.00025 ohm-cm
cured 30 min @ 120°C
0.00051 ohm-cm
0.00051 ohm-cm
cured 2 hrs @ 80°C
0.0041 ohm-cm
0.0041 ohm-cm
cured 24 hrs @ 65°C
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 150 °C
0.250 hour

@Temperature 302 °F
30.0 min

@Temperature 120 °C
0.500 hour

@Temperature 248 °F
300 - 420 min

@Temperature 80.0 °C
5.00 - 7.00 hour

@Temperature 176 °F
1440 min

@Temperature 65.0 °C
24.0 hour

@Temperature 149 °F
Descriptive Properties Value Comments
Color Silver
Thixotropic Index 4
Working Life days 2