Inno-Comp INNOPOL® CS 1-3250 42% Chalk-Filled Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 1-3250 42% Chalk-Filled Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 1-3250 is a 42% chalk-filled polypropylene homopolymer compound /PP-H KD42 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOL® CS 1-3250 is developed for producing injection molded components for household equipments.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.24 g/cc

@Temperature 23.0 °C
0.0448 lb/in³

@Temperature 73.4 °F
ISO 1183
Melt Flow 7.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Ash 24 %

@Temperature 900 °C
24 %

@Temperature 1650 °F
ISO 3451-1/A
Mechanical Properties Metric English Comments
Tensile Strength, Yield 25.0 MPa
3630 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 3.6 %
3.6 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
4.50 kJ/m²

@Temperature 23.0 °C
2.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-1,-2
Descriptive Properties Value Comments
Color Natural