- Shin-Etsu Silicones LIMSâ„¢ KEG2002-50A/B Elastomer
Shin-Etsu Silicones LIMSâ„¢ KEG2002-50A/B Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Shin-Etsu Silicones |
| Trade Name | LIMS™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shin-Etsu Silicones LIMSâ„¢ KEG2002-50A/B Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Shin-Etsu Silicones of America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | |
| Viscosity | 750000 cP | 750000 cP | A |
| 750000 cP | 750000 cP | B | |
| Linear Mold Shrinkage | 0.026 cm/cm | 0.026 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 51 | 51 | |
| Tensile Strength | 11.0 MPa | 1600 psi | |
| Elongation at Yield | 500 % | 500 % | |
| 100% Modulus | 0.00172 GPa | 0.249 ksi | |
| Tear Strength | 39.0 kN/m | 223 pli | |
| Compression Set | 7.0 % @Temperature 200 °C, Time 14400 sec |
7.0 % @Temperature 392 °F, Time 4.00 hour |
|
| 32 % @Temperature 150 °C, Time 3600 sec |
32 % @Temperature 302 °F, Time 1.00 hour |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 5.00 min @Temperature 150 °C |
0.0833 hour @Temperature 302 °F |
Press Cure |
| 60.0 min @Temperature 150 °C |
1.00 hour @Temperature 302 °F |
Post Cure |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Translucent | |
| Cure Rate | 28 | T10 (302°F, ODR) |
| 39 | T90 (302°F, ODR) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1980 TPE, PP Overmold or Standalone use
- SABIC B4660/B4660AB High Density Polyethylene for Blow Molding
- Covestro Apec® DP9-9331 High-Heat Polycarbonate, General Purpose (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP QCL34 PA6.10
- Borealis RA130E-1498 Polypropylene Random Copolymer
- Unifrax Fiberfrax® 6001-M-5 Kaolin Bulk Fiber
- Eastman Tenite Propionate 358A4000018 Clear, Trsp Cellulose Acetate Propionate
- Axiall 1751 Clear 7002 Flexible PVC
- Bulk Molding Compounds BMC 6241 Glass Reinforced BMC
- Industeel SOLEIL A2 13% Cr High Strength Martensitic Stainless Steel (QT650 Heat Treatment)
Copyright © lookpolymers.com All Rights Reserved