Mechanical Properties | Metric | English | Comments |
---|---|---|---|
100% Modulus | 0.00172 GPa | 0.249 ksi | ASTM D412 |
Network Polymers Softflex® 0921 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc. |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | |
Shin-Etsu Silicones LIMSâ„¢ KEG2002-50A/B Elastomer Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | |
Shin-Etsu Silicones LIMSâ„¢ KEG2000-50A/B Elastomer KEG2000-50 is a liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. Its viscosity is low enough to allow easy pum.. |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | Average |
Arlon Thermavac® 0.030" (0.762 mm) Uncured Silicone Vacuum Bagging (30400N030) Uncured, unsupported silicone rubber with a thickness of 0.030 in ± 0.003 (0.76 mm ± 0.038) on a Kodacel carrier (0.005 in., 0.13 mm nominal thickness); 0.003 in. (0.8 mm) polyethylene interleave... |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | Average |
Arlon Thermavac® 0.040" (0.762 mm) Cured Silicone Vacuum Bagging (10502R040) Unsupported cured/post cured silicone rubber with a thickness of 0.040 in. ±0.004 (1.0 mm ±0.10); 0.003 in. (0.8 mm) polyethylene interleave. The shelf life is defined as the duration of time for.. |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | Average |
Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502N060) Unsupported cured/post cured silicone rubber with a thickness of 0.060 in. ±0.006 (1.5 mm ±0.15 ); 0.003 in. (0.8 mm) polyethylene interleave. Color: Translucent. Weight: 2339 g/m² ± 234 (69.0.. |
|||
100% Modulus | 0.00172 GPa | 0.249 ksi | Average |
Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502R060) Unsupported cured/post cured silicone rubber with a thickness of 0.060 in. ±0.006 (1.5 mm ±0.15); 0.003 in. (0.8 mm) polyethylene interleave. The shelf life is defined as the duration of time for.. |