Samsung Cheil Industries Starex® GR-4020L ABS, Glass Filled

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® GR-4020L ABS, Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS/GF material that is used in printer LBP fuserInformation provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D785
Tensile Strength at Break 86.3 MPa
12500 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 88.3 MPa
12800 psi
5 mm/min; ASTM D638
Elongation at Break 2.5 %
2.5 %
5 mm/min; ASTM D638
Tensile Modulus 5.30 GPa
768 ksi
5 mm/min; ASTM D638
Flexural Strength 108 MPa
15700 psi
2.8 mm/min; ASTM D790
Flexural Modulus 5.30 GPa
768 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 0.667 J/cm

@Thickness 3.17 mm
1.25 ft-lb/in

@Thickness 0.125 in
ASTM D256
0.677 J/cm

@Thickness 6.35 mm
1.27 ft-lb/in

@Thickness 0.250 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 104 °C

@Thickness 6.40 mm
219 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 100 °C

@Thickness 6.40 mm
212 °F

@Thickness 0.252 in
ASTM D648
Vicat Softening Point 105 °C
221 °F
B/50; ISO R306
107 °C
225 °F
B/120; ISO R306
Flammability, UL94 HB

@Thickness 1.50 - 6.00 mm
HB

@Thickness 0.0591 - 0.236 in