| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR RC3 High Impact Polystyrene (HIPS)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,088-06-07-18 Special high impact, high gloss polystyrene grade. Suitable for injection molding in the appliances sector. Applications: Typical uses are domestic appliances, door handles and internal components of refrigerators, front panels of washing machines, point of sales, sanitary and houseware.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50 mm/min |
| Elongation at Break | 40 % | 40 % | Nominal |
| Elongation at Yield | 1.6 % | 1.6 % | 50 mm/min |
| Tensile Modulus | 1.95 GPa | 283 ksi | 1 mm/min |
| Charpy Impact Unnotched | 12.0 J/cm² | 57.1 ft-lb/in² | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | |
| Vicat Softening Point | 88.0 °C | 190 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 65.0 kV/mm | 1650 kV/in | |
| Dissipation Factor | 0.00030 @Frequency 100 Hz |
0.00030 @Frequency 100 Hz |
|
| Comparative Tracking Index | 575 V | 575 V |