NOVA Chemicals Sclair® 11C1 Octene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11C1 Octene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low gel, Good processability, Excellent mechanical propertiesApplications: Shrink filmAdditives: Process stabilizerFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D882
Film Elongation at Break, MD 540 %
540 %
ASTM D882
Film Elongation at Break, TD 990 %
990 %
ASTM D882
Secant Modulus, MD 0.165 GPa
23.9 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.170 GPa
24.7 ksi
at 1%; ASTM D882
Impact 125
125
J/mm; NOVA Chemicals Puncture test
Coefficient of Friction 0.70
0.70
ASTM D1894
Elmendorf Tear Strength, MD 24.0 g/micron
610 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 26.0 g/micron
660 g/mil
ASTM D1922
Dart Drop 8.00 g/micron
203 g/mil
F<sub>50</sub>, ASTM D1709/A
Film Tensile Strength at Break, MD 56.0 MPa
8120 psi
ASTM D882
Film Tensile Strength at Break, TD 47.0 MPa
6820 psi
ASTM D882
Optical Properties Metric English Comments
Haze 11 %
11 %
Optical properties are quoted prior to biaxial orientation; ASTM D1003
Gloss 58 %
58 %
at 45°; Optical properties are quoted prior to biaxial orientation; ASTM D2457