SCG Chemicals EL-Proâ„¢ P403J Polypropylene Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Pro™ |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SCG Chemicals EL-Proâ„¢ P403J Polypropylene Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics:High stiffnessHigh glossGood processabilityOdorlessSafe for food contactRecommended Applications:General purpose housewaresFood containersMedical instrumentsInfant articles, toysOffice accessoriesInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | ASTM D1505 |
| Linear Mold Shrinkage, Flow | 0.0137 cm/cm <br>@Thickness 2.00 mm |
0.0137 in/in <br>@Thickness 0.0787 in |
TPE Method |
| Linear Mold Shrinkage, Transverse | 0.0164 cm/cm <br>@Thickness 2.00 mm |
0.0164 in/in <br>@Thickness 0.0787 in |
TPE Method |
| Melt Flow | 3.5 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
3.5 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 1.32 GPa | 192 ksi | ASTM D790 |
| Izod Impact, Notched | 0.245 J/cm <br>@Temperature 0.000 °C |
0.459 ft-lb/in <br>@Temperature 32.0 °F |
ASTM D256 |
| 0.392 J/cm <br>@Temperature 23.0 °C |
0.735 ft-lb/in <br>@Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 155 °C | 311 °F | ASTM D1525 |
| Brittleness Temperature | -20.0 °C | -4.00 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 50 % <br>@Thickness 1.00 mm |
50 % <br>@Thickness 0.0394 in |
ASTM D1003 |
| Gloss | 65 % <br>@Thickness 1.00 mm |
65 % <br>@Thickness 0.0394 in |
ASTM D2457 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V70H Fluoroelastomer Compound
- LyondellBasell Petrothene® LR734011 High Density Polyethylene (Sheet & Profile Extrusion)
- Ipiranga Petrochem GV 0350 HDPE
- Haysite HCR-100 Corrosion Resistant Polyester/Glass Sheet
- Techmer ES HiFill® PA6/6 0177 B Nylon 66
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 35-HR-1 TPE
- A. Schulman POLYBATCH™ Opaque Blue 40356 Concentrate Based In LLDPE
- DuPont™ Kapton® 50HN Polyimide Film, 13 Micron Thickness
Copyright © lookpolymers.com All Rights Reserved