SABIC Innovative Plastics Lexan® ML7647K PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML7647K PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.26 %
0.26 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 52.0 MPa
7540 psi
Type I, 50 mm/min; ASTM D638
52.0 MPa
7540 psi
50 mm/min; ISO 527
Elongation at Break 94 %
94 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.3 %
5.3 %
50 mm/min; ISO 527
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
2.18 GPa
316 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
2 mm/min; ISO 178
87.0 MPa
12600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.13 GPa
309 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.16 GPa
313 ksi
2 mm/min; ISO 178
Izod Impact, Notched 7.70 J/cm
14.4 ft-lb/in
ASTM D256
7.20 J/cm

@Temperature -30.0 °C
13.5 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 57.0 kJ/m²
27.1 ft-lb/in²
80*10*4; ISO 180/1A
45.0 kJ/m²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 6.00 J/cm²
28.6 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 69.0 J

@Temperature 23.0 °C
50.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
74.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ASTM D1525
138 °C
280 °F
Rate B/50; ISO 306
138 °C
280 °F
Rate B/120; ISO 306