Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCY620HS PC+ABS PC+ ABS General Purpose Non-FR |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCY620S PC+ABS PC+ ABS Automotive applications |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® ML7647K PC (Asia Pacific) Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Faradex DS0036IC PC (Europe-Africa-Middle East) LNP* FARADEX* DS0036IC is a compound based on Polycarbonate resin, containing Stainless Steel Fiber, Flame Retardant. Added features include: Non-Brominated & Non-Chlorinated Flame Retardant, High I.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer (Asia Pacific) Opaque PC-Siloxane copolymer with excellent processability. UV stabilized. UL rated V-0/5VA/CTI-PLC-2. Available in limited colors. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 6.4 mm; ASTM D790 |
SABIC Innovative Plastics Lexan® FL405 PC Various weight reductions at 0.250"" (6.38 mm) wall. Impact resistant, superior processing, excellent surface. UL94 V-0 at 0.120 |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | ASTM D790 |
Covestro Apec® DP9-9333 High-Heat Polycarbonate, General Purpose, UV-Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | ASTM D790 |
Covestro Apec® DP9-9351 High-Heat Polycarbonate, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Flexural Yield Strength | 86.2 - 103 MPa | 12500 - 15000 psi | Average value: 91.6 MPa Grade Count:11 |
Overview of materials for Nylon 612, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Yield Strength | 86.3 MPa @Thickness 6.40 mm |
12500 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
LG Chemical Lupox® TE5000S PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Roof Rack)CAS No. 137050-02-03, 24968-12-5 and 103598-77-2Information provided.. |
|||
Flexural Yield Strength | 86.3 MPa @Thickness 3.20 mm |
12500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY HR5007AE PC/ABS, High Impact Description: Injection Molding, PC/ABS, High Flow, High ImpactApplication: E&E (Housing)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 86.3 MPa @Thickness 3.20 mm |
12500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY NS5000 PC/ABS, High Impact Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High ImpactApplication: Automotive (Interior)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS LNP LUBRICOMP* NL001 is a compound b ased on PC+ABS resin containing 5% PTFE. Added features include: Wear Resistant, Suitable for Thin Wall Applications. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WBG16 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Graphite.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Star Plastics PC1510FR Molding Grade PC Information provided by Star Plastics, Inc. |
|||
Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Star Plastics PC1510R Molding Grade PC Information provided by Star Plastics, Inc. |
|||
Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Star Plastics PC1510R Molding Grade PC with Release Information provided by Star Plastics, Inc. |
|||
Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
Star Plastics PC1510RUV Molding Grade PC Information provided by Star Plastics, Inc. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PVX0800 PPE NORYL* PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF742XXH PP LNP* THERMOCOMP* MF742XXH is a compound based on Polypropylene resin containing Glass Fiber and proprietary antimicrobial additives. This product is best suited for touch surfaces in healthcare app.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp MFM43S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFM43S is a compound based on Polypropylene resin containing Glass Fiber, Mineral. Added features include : Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2607 Polycarbonate, Injection Grade Easy flowing injection molding grade with easy mold release and UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially a.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2658 Polycarbonate, Injection Grade Easy flowing BgVV- and FDA injection molding grade with easy mold release, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer M.. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2858 Polycarbonate, Injection Grade Medium flowing BgVV- and FDA injection molding grade, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Flexural Yield Strength | 86.18 MPa | 12500 psi | |
Abatron AboCast/AboCure 8109-10 2-part, clear, slow casting/impregnating dielectric compound. Low dielectric constant, good flexibility and thermocycling properties. Abocast 8502-4 is a red (and other colors), filled version.Pro.. |
|||
Flexural Yield Strength | 86.2 - 132 MPa | 12500 - 19100 psi | Average value: 105 MPa Grade Count:7 |
Overview of materials for Polycarbonate, Glass Fiber & Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber & Bead Filled". Each property range of values reported is minimum and maximum.. |
|||
Flexural Yield Strength | 86.3 MPa | 12500 psi | ASTM D790 |
Samyang Trirex® 3026B Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3026B is an extrusion grade.Applications: BottlesInformation provided by Samyang. |
|||
Flexural Yield Strength | 86.0 MPa | 12500 psi | ASTM D790 |
Plaslok 308 Black (INJ) Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 308 is a two-stage, mineral and flock.. |