- Polymer Property : Melt Flow = 16 g/10 min
Polymer Property : Melt Flow = 16 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 16 g/10 min | 16 g/10 min | (Condition L) ASTM D-1238-94a |
| Multibase Multi-Flex® TPO D-5016 Multi-Flex® D-5016 is an elastomer modified polypropylene for applications requiring elastomeric properties and good molding behavior.Data provided by Multibase. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc.. |
|||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
16 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| SABIC Innovative Plastics Lexan® 910A PC (Europe-Africa-Middle East) LEXAN 910A is a low viscosity flame retardant grade, intended for electrical applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Melt Flow | 16 g/10 min | 16 g/10 min | Condition I; ASTM D1238 |
| Plaskolite Optix® PL-150 Acrylic Resin
(discontinued **) Injection/extrusion pellets.Data provided by the manufacturer, Plaskolite, Inc. |
|||
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Ineos ABS Lustran® H607AS Contains antistatic additives,Property data per ISO test methods. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| LG Chemical SEETEC M1500 Polypropylene Impact Copolymer SEETEC M1500 is a heterophasic polypropylene copolymer for injection molding applications. SEETEC M1500 exhibits a high flowability and a good balance of stiffness and impact strength. SEETEC M1500 .. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| LyondellBasell Hostacomâ„¢ TRC704D Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ TRC704D medium high melt flow, 1,500 MPa flexural modulus, UV-stabilized thermoplastic elastomeric olefin (TEO) resin has an excellent combination of properties and proce.. |
|||
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| SABIC Innovative Plastics ULTEM 1110 PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C). ECO Conforming. |
|||
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| SABIC Innovative Plastics Ultem MD131A PEI (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimide (Tg 217C). US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 380 °C |
16 g/10 min @Load 4.76 lb, Temperature 716 °F |
ASTM D1238 |
| Solvay Specialty Polymers Radel® R-7400 Polyphenylsulfone (PPSU) Radel® R-7300 (for light colors) and R-7400 (for darker colors) polyphenylsulfone resins were developed specifically for aircraft interior applications, and through the use of a proprietary flame.. |
|||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Star Plastics PC1510R Molding Grade PC with Release Information provided by Star Plastics, Inc. |
|||
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 250 °C |
16 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced Material with superior chemical resistance that can be used in the interior/exterior material of household appliances that require heat resistanceInformation provided by Samsung Cheil Industries. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Samyang Triloy® 210NH PC/ABS alloy, Flame Retardant Non-halogenCharacteristics:Impact resistantHeat resistantFlame retardantDimensional stabilityProcessabilityApplications:Cellular phoneMonitor housingCoffee makerHair dryerO/A partAll information pro.. |
|||
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 (Asia Pacific) NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL GTX GTX989 PPE+PA NORYL GTX989 is a conductive and high heat material, especially designed for in- and on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity.. |
|||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 266 °C |
16 g/10 min @Load 2.65 lb, Temperature 511 °F |
ASTM D1238 |
| SABIC Innovative Plastics Valox® 815F PBT+PET (Asia Pacific) PBT+PET, 15% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 4020 Concentrate Based In Polyethylene DescriptionPOLYBATCH® Blue 4020 is a blue color concentrate based in polyethylene. This concentrate was designed to provide intense blue color in polyolefin film and molding applications. POLYBA.. |
|||
| Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
| Melt Flow | 16 g/10 min | 16 g/10 min | ASTM D1238 |
| Tipco Tipcolene® HR 8234 - 10% Talc/Mineral Reinforced Polypropylene Copolymer, Very High Impact Strength & Flow 10% Mineral Reinforced, Very High Impact PP CopolymerApplications: Automotive BumpersProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Melt Flow | 16 - 24 g/10 min @Temperature 230 °C |
16 - 24 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 4020 Concentrate Based In Polyethylene DescriptionPOLYBATCH® Blue 4020 is a blue color concentrate based in polyethylene. This concentrate was designed to provide intense blue color in polyolefin film and molding applications. POLYBA.. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene DescriptionPOLYBATCH® P90062PF is an off-white color concentrate based in polypropylene. This concentrate was designed to provide color polypropylene film, extrusion, and molding applications. PO.. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Yellow 2450E Concentrate Based In Polyethylene DescriptionPOLYBATCH® 2450E is a yellow color concentrate base in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 2450E is he.. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5670 is a red color concentrate based in polyethylene. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 56.. |
|||
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm³/10min; ISO 1133 |
| DuPont Performance Polymers Rynite® RE5264 NC010 Polyethylene Terephthalate (PET)
(Unverified Data**) 36% Glass Reinforced Polyethylene Terephthalate Rynite RE5264 NC010 is a 36% glass fiber reinforced color stabilized modified polyethylene terephthalate.Information provided by DuPont Performance Po.. |
|||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Diamond Polymers PC-1500F Clear, Natural Polycarbonate Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Melt Flow | 16 g/10 min | 16 g/10 min | ISO 1133 |
| Addiplast Addilene H 560 Polypropylene Homopolymer High heat resistance, detergent stabilized, anti-yellowingInformation provided by Addiplast. |
|||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 190 °C |
16 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene DescriptionPOLYBATCH® P80515PF is a color matched white color concentrate based in polypropylene. This concentrate was designed to provide opacity and color in polypropylene film, extrusion, and m.. |
|||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
16 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| SABIC Innovative Plastics Lexan® ML6240 PC Copolymer (Europe-Africa-Middle East) Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Europe-Africa-Middle Eas.. |
|||
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Bhansali Engineering Abstron IMGS20 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||