SABIC Innovative Plastics LNP Thermocomp RX06423 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RX06423 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX06423 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ASTM D 792 |
| 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm @Time 86400 sec |
0.0037 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0095 cm/cm @Time 86400 sec |
0.0095 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 218 MPa | 31600 psi | ASTM D 638 |
| 225 MPa | 32600 psi | ISO 527 | |
| Tensile Strength, Yield | 218 MPa | 31600 psi | ASTM D 638 |
| 225 MPa | 32600 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D 638 |
| 2.1 % | 2.1 % | ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D 638 |
| 2.1 % | 2.1 % | ISO 527 | |
| Tensile Modulus | 21.1 GPa | 3060 ksi | 1 mm/min; ISO 527 |
| 22.06 GPa | 3200 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 317 MPa | 46000 psi | ASTM D 790 |
| 340 MPa | 49300 psi | ISO 178 | |
| Flexural Modulus | 17.92 GPa | 2599 ksi | ASTM D 790 |
| 19.0 GPa | 2760 ksi | ISO 178 | |
| Izod Impact, Notched | 1.22 J/cm @Temperature 23.0 °C |
2.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 11.69 J/cm @Temperature 23.0 °C |
21.90 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 16.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.89 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 16.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 237 °C | 459 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 245 °C @Thickness 3.20 mm |
473 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 232 °C @Thickness 3.20 mm |
450 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |