SABIC Innovative Plastics LNP THERMOCOMP DF0089 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP DF0089 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* DF0089 is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Flame Retardant.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
1.589 g/cc
0.05741 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527
131 MPa
19000 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 12.4 GPa
1800 ksi
1 mm/min; ISO 527
13.72 GPa
1990 ksi
50 mm/min; ASTM D638
Flexural Strength 190 MPa
27600 psi
ASTM D790
203 MPa
29400 psi
ISO 178
Flexural Modulus 11.79 GPa
1710 ksi
ASTM D790
12.5 GPa
1810 ksi
ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
 279 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 UL 94 by SABIC-IP