Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 13.7 GPa | 1990 ksi | Conditioned; ASTM D638 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA)
(Unverified Data**) Amodel AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrar.. |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | |
Idemitsu Kosan Xarec® WA 214 SPS, 40% Glass Filled |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | |
Idemitsu Kosan Xarec® WA 214LG SPS, 40% Glass Filled Crystalline Polymer, Glass Filled |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | ASTM D638 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) Amodel® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in.. |
|||
Tensile Modulus | 13.72 GPa | 1990 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF0089 PC LNP THERMOCOMP* DF0089 is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Flame Retardant. |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon DE0049 PC (Europe-Africa-Middle East) LNP* Stat-kon* DC-1004 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.This.. |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | 1 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 126F9 Nylon 6, 45% Glass Fiber SAXAMID 126F9 is a polyamide 6 injection-molding-grade reinforced with 45% glass fibers.Information provided by SAX Polymers |
|||
Tensile Modulus | 13.7 GPa | 1990 ksi | ISO 527 |
Polyram RamSter PF300G9 PBT, 45% Glass Fiber 45% Glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |