SABIC Innovative Plastics LNP STAT-KON DX01303C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX01303C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00070 cm/cm @Time 86400 sec |
0.00070 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527 |
| 118 MPa | 17100 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 2.1 % | 2.1 % | ASTM D638 | |
| Tensile Modulus | 9.23 GPa | 1340 ksi | 50 mm/min; ASTM D638 |
| 9.38 GPa | 1360 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 179 MPa | 26000 psi | ISO 178 |
| 192 MPa | 27800 psi | ASTM D790 | |
| Flexural Modulus | 8.35 GPa | 1210 ksi | ISO 178 |
| 8.79 GPa | 1270 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 46.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 - 1.00e+7 ohm | 1000 - 1.00e+7 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S2E Silver-Coated Solid Glass Spheres
- Premix Thermoplastics PRE-ELEC® ESD 5350 Static Dissipative Thermoplastic Compound
- Parker Chomerics CHO-SEAL 1239 Conductive Elastomer
- Polymer Resources PPX/NY G30 PPO/Nylon 66 Alloy , 30% Glass Reinforced
- Humiseal 1B31 Acrylic Conformal Coating
- SABIC Innovative Plastics ULTEM HU2100 PEI
- Solvay MIRATAINE® CAB-A Surfactant
- Shinkong Synthetic Fibers Shinite® E202G30 PBT, 30% Glass Filled
- Chase Plastics CP Pryme® N120GL (DAM) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated
- BNZ Materials Marinite® A Ceramic Board for Aluminum Contact
Copyright © lookpolymers.com All Rights Reserved