Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Flexural Strength = 27800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 192 MPa
27800 psi
Plastcom SLOVAMID 6 NG1 GF 20 HLS PA6, 20% glass fibre, combined stability
FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre, heat and wheather stabilized. Stabilized against hydrolisys. Good surface finisch. Scratch resistent.Packaging, tra..
Flexural Strength 192 MPa
27800 psi
ASTM D790
Network Polymers Nylon 6G20L
Description: Natural NylonInformation provided by Network Polymers Inc.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC
LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated.
Flexural Strength 192 MPa
27800 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP IFL36L PA6.12
LNP* LUBRICOMP* IFL36L is a compound based on Nylon 6/12 containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Low Extractable, Wear Resistant.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 (Europe-Africa-Middle East)
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP Lubriloy RF206H PA 66
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant, Lubricants. Added features of this material include: Internally Lubricated.This data was su..
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206H PA 66 (Asia Pacific)
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Lubricants, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206XXH PA 66
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare
Flexural Strength 192 MPa
27800 psi
ASTM D790
SABIC Innovative Plastics LNP STAT-KON DX01303C PC
LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DC006H PC
LNP* THERMOCOMP* DC006H is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DC006H PC (Asia Pacific)
LNP* Thermocomp* DC006H is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific)
LNP* THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing Glass Fiber.
Flexural Strength 192 MPa
27800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF006 is a compound based on Polyethersulfone resin containing Glass Fiber.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend
LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF406XXX PPO Blend (Asia Pacific)
LNP THERMOCOMP* ZF406XXX is a compound based on PPO Blend resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant.
Flexural Strength 192 MPa
27800 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP HF008 PA11
LNP THERMOCOMP* HF008 is a compound based on Nylon 11 resin containing 40% Glass Fiber.
Flexural Strength 192 MPa
27800 psi
ASTM D790
PolyOne Stat-Tech™ NJ-20CF/000 Black Polyamide 12 (Nylon 12)
Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Strength 192 MPa
27800 psi
ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES
LNP* THERMOCOMP* JF006EXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Flexural Strength 192 MPa
27800 psi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL FE1630PW PPE+PS (Europe-Africa-Middle East)
Noryl* FE1630PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid en..