- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 509 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 509 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | |
| LATI Larton GK/400 PPS, Glass/Carbon Fiber Reinforced Polyphenylene Sulfide (PPS) based compound. Glass fibers / Carbon fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa &.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear (Asia Pacific) LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP OX97635 PPS LNP LUBRICOMP* OX97635 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® BR111BL Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® BR111BL Ryton® BR111 is a black-colored glass fiber and mineral filled polyphenylene sulfide compound that provides enhanced mechanical strength with good electrical properties and outs.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® BR42B Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® BR42B 40% glass fiber reinforced polyphenylene sulfide compound is specially formulated to provide low coefficient of friction and reduced wear rate for use in applications requiring low s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4-02 Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4 and R-4-02 40% glass fiber reinforced polyphenylene sulfide compounds provide a good combination of mechanical and electrical properties with outstanding chemical resistance, even at e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipmentFeat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4-200NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipmentFeat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4-240BL Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-4XT Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4XT and R-4-02XT 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength with good electrical properties and outstanding chemical resistance, even.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-7-120BL Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® R-7-120NA and R-7-120BL glass fiber and mineral filled polyphenylene sulfide compounds provide good strength and low maintenance molding using conventional molding equipment.Features: Good.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-7-120NA Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® R-7-120NA and R-7-120BL glass fiber and mineral filled polyphenylene sulfide compounds provide good strength and low maintenance molding using conventional molding equipment.Features: Good.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ryton® R-7-121NA Polyphenylene Sulfide (PPS), GlassMineral Filled Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional moldin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | GB/T 1634.2-2004 |
| Sichuan Deyang Haton® hGR302 PPS / F4 Polyphenylene Sulfide Injection molding, anti-frictionInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS - Linear (Europe-Africa-Middle East) LNP* THERMOCOMP* OF008E is a compound based on PPS - Linear resin containing Glass Fiber. Added features include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP UX06032 PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UX06032 is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp OFJ66 PPS - Linear (Asia Pacific) LNP* Thermocomp* OFJ66 is a compound based on PPS - Linear resin containing Glass Fiber, Mineral. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Asi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT2VZ-15H PA6T/66-GF15 Information provided by EMS Grivory |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® XE 4101 black 9225 PA*-GF40 Product description: Grivory XE 4101 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® HTN 51G45HSL BK083 Polyphthalamide (PPA)
(Unverified Data**) 45% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G45HSL BK083 is a 45% glass reinforced heat stabilized lubricated high performance polyamide resin. It is also a PPA resin.Information .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | ISO 75-1/-2 |
| Barlog Plastics KEBATRON C2040G5 PPS, cross-linked, 40% GF, reduced residual chlorine PPS-GF40Information provided by BARLOG plastics GmbH. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | Unannealed; ASTM D648 |
| LNP Lubricomp® OCL-4534 EM Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant
(discont Features: Good Moldability, LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP g.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America FM 4008 Fiberglass and Mineral Reinforced Phenolic Resole FM 4008 is a fiberglass and mineral reinforced phenolic resole compound, with excellent dimensional stability and good strength at elevated temperatures. Information supplied by Sumitomo Bak North A.. |
|||