Reliance Industries PVAXX H65

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic
Manufacturer	Reliance Industries
Trade Name	PVAXX
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Reliance Industries PVAXX H65.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The key property of all PVAXX polymer is this product`s unique capacity to biodegrade into non-toxic residues under both aerobic and non-aerobic conditions.Information provided by Reliance Industries

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³	ASTM D792
Melt Flow	4.1 g/10 min @Load 2.16 kg, Temperature 210 °C	4.1 g/10 min @Load 4.76 lb, Temperature 410 °F

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	102	102	ASTM D 785
Tensile Strength, Ultimate	46.0 MPa	6670 psi	ASTM D638
Tensile Strength, Yield	46.5 MPa	6740 psi	ASTM D368
Elongation at Break	19 %	19 %	ASTM D638
Elongation at Yield	15 %	15 %	ASTM D638
Tensile Modulus	0.530 GPa	76.9 ksi	ASTM D638
Flexural Strength	27.4 MPa	3970 psi	2mm Deflection; ASTM D790
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
Izod Impact, Notched (ISO)	1.28 kJ/m²	0.609 ft-lb/in²	ASTM D256
Izod Impact, Unnotched (ISO)	12.2 kJ/m²	5.81 ft-lb/in²	ASTM D256
Charpy Impact Unnotched	0.728 J/cm²	3.46 ft-lb/in²	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	216 °C	421 °F	DSC Peak
Deflection Temperature at 1.8 MPa (264 psi)	69.0 - 73.0 °C	156 - 163 °F	ASTM D648
Vicat Softening Point	200 °C	392 °F	ASTM D1525
Oxygen Index	17.5 %	17.5 %

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm
Surface Resistance	3.50e+14 ohm	3.50e+14 ohm