Ravago Manufacturing Americas Hylex® P1010L Polycarbonate, Unreinforced, Intermediate Flow
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1010L Polycarbonate, Unreinforced, Intermediate Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24-Hr Immersion; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength | 69.6 MPa | 10100 psi | ASTM D638 |
| Elongation at Break | 115 % | 115 % | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm |
15.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Vicat Softening Point | 154 °C | 310 °F | ASTM D1525 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
||
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.585 | 1.585 | ASTM D542 |
| Haze | 0.50 - 0.80 % @Thickness 3.17 mm |
0.50 - 0.80 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 89 - 91 % @Thickness 3.17 mm |
89 - 91 % @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm @Thickness 3.17 mm |
410 kV/in @Thickness 0.125 in |
in Air; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® LG8002 PC+ABS (Asia Pacific)
- Kolon DIAMAT® IG
- Techmer ES Plastiblend® PC/ABS 8800
- Chicago Extruded Metals UNS C48200 Copper-Zinc-Tin Alloy
- Arkema Group Orgalloy® RS 6020 Nylon 6 Alloy, 20% Glass Fiber (Conditioned)
- Solvay RHODOLINE® 640 Surfactant
- Arlon 30600R010 0.010" (0.254 mm) Uncured/Unsupported Silicone Rubber on a Release Carrier
Copyright © lookpolymers.com All Rights Reserved