Radici Radilon® S CV300 (dry) Nylon 6

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Radilon® S CV300 (dry) Nylon 6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.34 g/cc	1.34 g/cc
Water Absorption	9.0 %	9.0 %
Moisture Absorption at Equilibrium	2.7 %	2.7 %
Viscosity Measurement	140	140	cm³/g Viscosity Number

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	70.0 MPa	10200 psi
Elongation at Break	11 %	11 %	Nominal
Elongation at Yield	3.0 %	3.0 %
Tensile Modulus	4.25 GPa	616 ksi
Charpy Impact Unnotched	3.00 J/cm² @Temperature -30.0 °C	14.3 ft-lb/in² @Temperature -22.0 °F
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F
Charpy Impact, Notched	0.200 J/cm² @Temperature -30.0 °C	0.952 ft-lb/in² @Temperature -22.0 °F
	0.310 J/cm² @Temperature 23.0 °C	1.48 ft-lb/in² @Temperature 73.4 °F

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F
Deflection Temperature at 0.46 MPa (66 psi)	170 °C	338 °F
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F
Vicat Softening Point	200 °C @Load 5.10 kg	392 °F @Load 11.2 lb	50°C/h
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm