Polyram RamLloy B001 Nylon 6/Polyolefin Alloy, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy B001 Nylon 6/Polyolefin Alloy, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6/Polyolefin alloy, reduction of water absorption, impact modified, for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.05 g/cc | 0.0372 - 0.0379 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 3.3 % | 3.3 % | ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 235 °C |
10 g/10 min @Load 22.0 lb, Temperature 455 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 180 % | 180 % | ISO 527 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | ISO 180 |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |