PolyOne Lubri-Tech™ AS-000/10T-2S ABS - 10% PTFE - 2% Silicone  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), PTFE Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ AS-000/10T-2S ABS - 10% PTFE - 2% Silicone  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ASTM D792
Water Absorption 0.19 %
0.19 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 3.17 mm
 0.0040 - 0.0060 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.0 MPa
5950 psi
ASTM D638
Elongation at Break 2.0 - 5.0 %
2.0 - 5.0 %
ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
ASTM D638
Flexural Yield Strength 41.0 MPa
5950 psi
ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
ASTM D790
Izod Impact, Notched 0.800 - 1.33 J/cm

@Thickness 6.35 mm
 1.50 - 2.49 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Processing Properties Metric English Comments
Melt Temperature 216 - 243 °C
421 - 469 °F
Stock
Mold Temperature 49.0 - 66.0 °C
120 - 151 °F
Drying Temperature 60.0 - 71.0 °C
140 - 160 °F