PolyOne Geon™ Vinyl Rigid Extrusion 87759 Polyvinyl Chloride, Rigid (PVC, Rigid)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Vinyl Rigid Extrusion 87759 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Note: Finished part testing is required for ASTM E-84 certification. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.45 g/cc	1.45 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	80	80	15 sec; ASTM D2240
Tensile Strength, Yield	40.6 MPa	5890 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.90 GPa	421 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	69.6 MPa	10100 psi	ASTM D790
Flexural Modulus	2.71 GPa	393 ksi	ASTM D790
Izod Impact, Notched	1.90 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.56 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
	2.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.75 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Compression Molded, Across Flow; ASTM D256A
	2.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	4.31 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Compression Molded, Flow; ASTM D256A
Dart Drop Total Energy	53.4 J/cm @Temperature 23.0 °C	0.100 ft-lb/mil @Temperature 73.4 °F	Procedure A, C.125; ASTM D4226
	66.7 J/cm @Temperature 23.0 °C	0.125 ft-lb/mil @Temperature 73.4 °F	Procedure B, C.125; ASTM D4226

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C	38.9 µin/in-°F	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	67.8 °C @Thickness 3.18 mm	154 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	ALL; UL 94

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 193 °C	360 - 379 °F

Descriptive Properties	Value	Comments
Agency Ratings	ASTM E 84
Ease of Sizing	Good
Features	Low Smoke Emission
Forms	Pellets
Generic Material	PVC, Rigid
Generic Name	Polyvinyl Chloride, Rigid (PVC, Rigid)
Processing Method	Extrusion
PVC Cell Classification	13253	ASTM D1784
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Profiles