Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 67.8 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 3.18 mm
154 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion 87350 Polyvinyl Chloride, Rigid (PVC, Rigid)
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 3.18 mm
154 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion 87759 Polyvinyl Chloride, Rigid (PVC, Rigid)
Note: Finished part testing is required for ASTM E-84 certification. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by Po..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 3.18 mm
154 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion 87850 Polyvinyl Chloride, Rigid (PVC, Rigid)
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 3.18 mm
154 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion L0111 Polyvinyl Chloride, Rigid (PVC, Rigid)
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 3.18 mm
154 °F

@Thickness 0.125 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Extrusion L0189 Polyvinyl Chloride, Rigid (PVC, Rigid)
All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high ..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 6.35 mm
154 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding MR200 Polyvinyl Chloride, Rigid (PVC, Rigid)
Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 6.35 mm
154 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne Geon™ Vinyl Rigid Molding MR201 Polyvinyl Chloride, Rigid (PVC, Rigid)
Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C

@Thickness 6.35 mm
154 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne LubriOne™ NN-000/10T-2S Black Polyamide 66 (Nylon 66)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
RheTech Products HP531-00 22% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
Applications: IP structural componentsAir ducts - distributionA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
RheTech Products HP531-680UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, BJAA Light Parchment
Applications: I/P componentsInterior trimA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
RheTech Products HP531-01UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
Applications: IP structural componentsAir ducts - distributionA/B/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
RheTech Products HP531-678UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, IT3A Medium Light Stone
Applications: I/P componentsInterior trimA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
RheTech Products HP531-679UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, 2B5A Black Ink
Applications: I/P componentsInterior trimA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
Kostat ICP-STAT ICS-1003 PS Sheet
KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
Kostat ICP-STAT ICD-1003 PS Sheet
KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
Diamond Polymers ABS VP-12
Description: Flame Retardant with UVInformation provided by Diamond Polymers, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D-648
Axiall 7450 Rigid PVC, Extrusion
Georgia Gulf 7450 is a special purpose rigid PVC extrusion compound designed for applications requiring the following properties: Excellent ToughnessSatin Surface AppearanceColorabilityChemical Res..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D-648
Axiall 7456 Rigid PVC, Extrusion
Georgia Gulf 7456 is a special purpose rigid PVC extrusion compound designed for applications requiring the following properties: ToughnessWeatherabilityWeldabilityChemical ResistanceEase of Proces..
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
Aclo Accutech Polypropylene Copolymer CP0436T40L1 Talc Reinforced
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
Aclo Accutech Polypropylene Copolymer CP0437M40CL Mica Reinforced Coupled
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
Aclo Accutech Polypropylene Homopolymer HP0339W20L1 Wollastonite Reinforced
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
annealed; ASTM D-648
Axiall 8266 Natural 02 Rigid PVC, Extrusion, Natural 02
Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
annealed; ASTM D-648
Axiall 8266 Rigid PVC, Extrusion
Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
annealed; ASTM D-648
Axiall 8266 Rigid PVC, Extrusion, Natural
Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
annealed; ASTM D-648
Axiall 8266 Rigid PVC, Extrusion, White
Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
Aclo Accutech Polypropylene Homopolymer HP0339T20L1 Talc Reinforced
Deflection Temperature at 1.8 MPa (264 psi) 67.8 - 95.0 °C
154 - 203 °F
Average value: 82.1 °C Grade Count:19
Overview of materials for Polystyrene, Extrusion Grade
This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Extrusion Grade". Each property range of values reported is minimum and maximum values of a..