Kingfa PA66-T15 15% Mineral Filled PA66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PA66-T15 15% Mineral Filled PA66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Good size stabilityLow tendency to wrapGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower toolsSport applianceInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc

@Temperature 23.0 °C
1.24 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.011 - 0.014 cm/cm

@Temperature 23.0 °C
0.011 - 0.014 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength at Break 55.0 MPa
7980 psi
10mm/min; ASTM D638
Elongation at Break >= 20 %
>= 20 %
10mm/min; ASTM D638
Flexural Strength 78.0 MPa
11300 psi
2mm/min; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.55 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.90 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 235 °C

@Thickness 6.40 mm
455 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 175 °C

@Thickness 6.40 mm
347 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 310 °C
<= 590 °F
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Start Point: 265°C
Middle Barrel Temperature 265 - 300 °C
509 - 572 °F
Start Point: 285°C
Front Barrel Temperature 275 - 305 °C
527 - 581 °F
Start Point: 285°C
Melt Temperature 275 - 310 °C
527 - 590 °F
Start Point: 285°C
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Start Point: 60°C
Drying Temperature 90.0 - 110 °C

@Time 14400 - 21600 sec
194 - 230 °F

@Time 4.00 - 6.00 hour
Pre-dry
Descriptive Properties Value Comments
Injection Speed Moderate to High
Mineral Content (%) 15