Polymer Property : Izod Impact, Notched = 2.30 J/cm Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Izod Impact, Notched 2.30 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded, Flow; ASTM D256A
PolyOne Geon™ Vinyl Rigid Extrusion 87759 Polyvinyl Chloride, Rigid (PVC, Rigid)
Note: Finished part testing is required for ASTM E-84 certification. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by Po..
Izod Impact, Notched 2.30 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded, Across Flow; ASTM D256A
PolyOne Geon™ Vinyl Rigid Extrusion L0660 Polyvinyl Chloride, Rigid (PVC, Rigid)
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Izod Impact, Notched 2.30 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Compression Molded, Flow; ASTM D256A
PolyOne Geon™ Vinyl Rigid Extrusion L9630 Polyvinyl Chloride, Rigid (PVC, Rigid)
Product can meet UL-94V-0. Material passed V-0 @ 1.5mm in screening test at PDI.Information provided by PolyOne
Izod Impact, Notched 2.30 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Premix Thermoplastics PRE-ELEC® PC/ABS 1420
PRE-ELEC PC/ABS 1420 is a conductive thermoplastic compound based on a PC/ABS blend. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PR..
Izod Impact, Notched 2.30 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Premix Thermoplastics PRE-ELEC® PE 1291
PRE-ELEC PE 1291 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129..
Izod Impact, Notched 2.30 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256, ISO 180/4a
EPICHEM Epiryl B PPO Polyphenylene oxide
Izod Impact, Notched 2.30 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Asahi Kasei Xyron® 300Z Modified Polyphenylene Ether
Flame RetardantInformation provided by Asahi Kasei
Izod Impact, Notched 2.30 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Asahi Kasei Xyron® 340W Modified Polyphenylene Ether
Flame RetardantInformation provided by Asahi Kasei
Izod Impact, Notched 2.30 J/cm

@Thickness 6.35 mm
4.30 ft-lb/in

@Thickness 0.250 in
ASTM D-256
Axiall 3121 Rigid PVC, Extrusion
Georgia Gulf 3121 is an exterior grade powder compound formulated for processing applications requiring high production output rate. Having excellent weatherability and impact strength, 3121 is sui..
Izod Impact, Notched 2.30 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
4.31 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Asahi Kasei Xyron® 300V Modified Polyphenylene Ether
Flame RetardantInformation provided by Asahi Kasei