Permabond 735 Cyanoacrylate, toughened

Category Polymer , Adhesive , Thermoset , Acrylic/Cyanoacrylate Adhesive
Manufacturer Permabond
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Permabond 735 Cyanoacrylate, toughened.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PERMABOND® 735 is a toughened cyanoacrylate with very good impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable over the shelf life of the product. This provides consistent performance. The product adheres to a variety of surfaces including steel, aluminum, galvanized steel, plastics and elastomers. Features & Benefits: Longer cure allows accurate alignment Toughened and flexible Ease of use – no mixing or heat cure Black - so suitable for dark surfaces 100% reactive, no solvents Information provided by Permabond.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Uncured
Viscosity 100 - 200 cP

@Temperature 25.0 °C
100 - 200 cP

@Temperature 77.0 °F
Uncured
Storage Temperature 2.00 - 7.00 °C
35.6 - 44.6 °F
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
ISO 868
Adhesive Bond Strength >= 5.00 MPa
>= 725 psi
PC, Substrate Failure, Shear; ISO 4587
>= 6.00 MPa
>= 870 psi
ABS, Substrate Failure, Shear; ISO 4587
>= 6.00 MPa
>= 870 psi
PVC, Substrate Failure, Shear; ISO 4587
13.0 - 15.0 MPa
1890 - 2180 psi
Aluminum, Shear; ISO 4587
24.0 - 30.0 MPa
3480 - 4350 psi
Steel, Shear; ISO 4587
Impact 5.0 - 10
5.0 - 10
kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950
Peel Strength 1.60 - 2.40 kN/m
9.13 - 13.7 pli
ASTM D903
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
Thermal Conductivity 0.100 W/m-K
0.694 BTU-in/hr-ft²-°F
Electrical Properties Metric English Comments
Dielectric Constant 2.5

@Frequency 10000 Hz
2.5

@Frequency 10000 Hz
Dielectric Strength 25.0 kV/mm
635 kV/in
Processing Properties Metric English Comments
Cure Time 0.0833 - 0.167 min
0.00139 - 0.00278 hour
Phenolic, handling time
0.167 - 0.250 min
0.00278 - 0.00417 hour
Buna N Rubber, handling time
0.500 - 0.833 min
0.00833 - 0.0139 hour
Steel, handling time
0.583 - 0.833 min
0.00972 - 0.0139 hour
Aluminum, handling time
1440 min
24.0 hour
full strength
Descriptive Properties Value Comments
Appearance Black
Uncured
Maximum Gap Fill (mm) 0.15
Strength Retention 10% at 150°C
Relative to 0°C
100% at 0°C
Relative to 0°C
50% at 100°C
Relative to 0°C
75% at -50°C
Relative to 0°C
90% at 50°C
Relative to 0°C