Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 105 Cyanoacrylate, for difficult rubbers PERMABOND® 105 is a low viscosity high purity cyanoacrylate adhesive. It is ideal for use on hard-to-bond plastics and rubbers such as natural rubber, EPDM and butyl rubber. Cyanoacrylate adhesives.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Buna N Rubber, handling time |
Permabond 2010 Cyanoacrylate, gap filling PERMABOND 200 is a high viscosity product with good flow control useful in wire tacking applications or bonding components. It is fast setting and suitable for use on plastics, rubber and metals. Cy.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Buna N Rubber, handling time |
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic, handling time |
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 2050 Cyanoacrylate, flexible PERMABOND® 2050 is a flexible cyanoacrylate adhesive, exhibiting improved peel strengths when compared to other grades. It has excellent impact and vibration resistance, and is suitable for bonding.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Buna Rubber, set time, cured |
Permabond 738 Cyanoacrylate, toughened PERMABOND 738 is a toughened cyanoacrylate with improved impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable over.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 940 Cyanoacrylate, low odor PERMABOND 940 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic resin, handling time |
Permabond 940 Cyanoacrylate, low odor PERMABOND 940 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | ABS, handling time |
Permabond 940 Cyanoacrylate, low odor PERMABOND 940 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 102 Cyanoacrylate, General purpose PERMABOND® 102 is a low viscosity general purpose cyanoacrylate adhesive suitable for bonding close-fitting components. It is fast setting and suitable for use on plastics, rubber and metals. Cyano.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Buna N Rubber, handling time |
Permabond 801 Cyanoacrylate, High Temperature PERMABOND® 801 is a low viscosity modified ethyl cyanoacrylate suitable for applications where high temperature resistance is required. This material is fast setting and has good adhesion to rubber.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic, handling time |
Permabond 802 Cyanoacrylate, High Temperature PERMABOND® 802 is a low viscosity modified ethyl cyanoacrylate suitable for applications where high temperature resistance is required. This material is fast setting and has good adhesion to rubber.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Buna N Rubber, handling time |
Permabond 820 Cyanoacrylate, High Temperature PERMABOND® 820 is a low viscosity modified ethyl cyanoacrylate suitable for applications where high temperature resistance is required. This material is fast setting and has good adhesion to rubber.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic, handling time |
Permabond 820 Cyanoacrylate, High Temperature PERMABOND® 820 is a low viscosity modified ethyl cyanoacrylate suitable for applications where high temperature resistance is required. This material is fast setting and has good adhesion to rubber.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic, handling time |
Permabond 920 Cyanoacrylate, High temperature PERMABOND® 920 is the original allyl cyanoacrylate adhesive. It is a single part, low viscosity liquid that will cure rapidly at room temperature when pressed into a thin film between parts. PERMAB.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic, set time |
Permabond 930 Cyanoacrylate PERMABOND 930 is a low odor, nonfogging, nonfrosting cyanoacrylate. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated. The .. |
|||
Cure Time | 0.0833 - 0.250 min | 0.00139 - 0.00417 hour | 10-20 mil thick layers cured with Dymax 5000-EC at 2 inches. Thicker layers may require more cure time. |
Dymax 9001v3.01 Resilient Clear Microencapsulant High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9001v3.01 Resilient Clear MicroencapsulantLowest stress potting and encapsulation on ceramic, FR-4 or flexible PCBs .. |
|||
Cure Time | 0.0333 - 0.250 min | 0.000556 - 0.00417 hour | 10-20 mil thick layers cured with Dymax 5000-EC at 2 inches. Thicker layers may require more cure time. |
Dymax 9001v3.1 Resilient, Low Modulus Clear Microencapsulant High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9001v3.1 Resilient, Low Modulus Clear MicroencapsulantLowest stress potting and encapsulation on ceramic, FR-4 or fl.. |
|||
Cure Time | 0.0833 - 0.250 min | 0.00139 - 0.00417 hour | 10-20 mil thick layers cured with Dymax 5000-EC at 2 inches. Thicker layers may require more cure time. |
Dymax 9003v3.0 Flexible Clear Microencapsulant High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9003v3.0 Flexible Clear MicroencapsulantGlob top for photosensing devices Cure Type: UV/Visible Typical Use: Optic.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Steel, handling time |
Permabond 941 Cyanoacrylate, low odor PERMABOND 941 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Aluminum, handling time |
Permabond 941 Cyanoacrylate, low odor PERMABOND 941 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | PVC, handling time |
Permabond 941 Cyanoacrylate, low odor PERMABOND 941 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic resin, handling time |
Permabond 941 Cyanoacrylate, low odor PERMABOND 941 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | ABS, handling time |
Permabond 941 Cyanoacrylate, low odor PERMABOND 941 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Aluminum, handling time |
Permabond 943 Cyanoacrylate, low odor PERMABOND 943 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Aluminum, handling time |
Permabond 947 Cyanoacrylate, low odor PERMABOND 947 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | PVC, handling time |
Permabond 947 Cyanoacrylate, low odor PERMABOND 947 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | Phenolic resin, handling time |
Permabond 947 Cyanoacrylate, low odor PERMABOND 947 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |
|||
Cure Time | 0.167 - 0.250 min | 0.00278 - 0.00417 hour | ABS, handling time |
Permabond 947 Cyanoacrylate, low odor PERMABOND 947 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad.. |