Polymer Property : Cure Time = 0.167 min Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, handling time
Permabond 101 Cyanoacrylate, Wicking Viscosity PERMABOND® 101 is a low viscosity product useful in wicking or penetrating applications or bonding closely fitting parts. It is fast setting and suitable for use on plastics, rubber and metals. Cya..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, handling time
Permabond 105 Cyanoacrylate, for difficult rubbers PERMABOND® 105 is a low viscosity high purity cyanoacrylate adhesive. It is ideal for use on hard-to-bond plastics and rubbers such as natural rubber, EPDM and butyl rubber. Cyanoacrylate adhesives..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, handling time
Permabond 105 Cyanoacrylate, for difficult rubbers PERMABOND® 105 is a low viscosity high purity cyanoacrylate adhesive. It is ideal for use on hard-to-bond plastics and rubbers such as natural rubber, EPDM and butyl rubber. Cyanoacrylate adhesives..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	PVC, handling time
Permabond 105 Cyanoacrylate, for difficult rubbers PERMABOND® 105 is a low viscosity high purity cyanoacrylate adhesive. It is ideal for use on hard-to-bond plastics and rubbers such as natural rubber, EPDM and butyl rubber. Cyanoacrylate adhesives..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	ABS, handling time
Permabond 105 Cyanoacrylate, for difficult rubbers PERMABOND® 105 is a low viscosity high purity cyanoacrylate adhesive. It is ideal for use on hard-to-bond plastics and rubbers such as natural rubber, EPDM and butyl rubber. Cyanoacrylate adhesives..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, handling time
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, handling time
Permabond 2011 Cyanoacrylate, gel PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, handling time
Permabond 2050 Cyanoacrylate, flexible PERMABOND® 2050 is a flexible cyanoacrylate adhesive, exhibiting improved peel strengths when compared to other grades. It has excellent impact and vibration resistance, and is suitable for bonding..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	PVC, handling time
Permabond 2050 Cyanoacrylate, flexible PERMABOND® 2050 is a flexible cyanoacrylate adhesive, exhibiting improved peel strengths when compared to other grades. It has excellent impact and vibration resistance, and is suitable for bonding..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, handling time
Permabond 268 Cyanoacrylate, General purpose PERMABOND® 268 is a medium-high viscosity cyanoacrylate for large gap fill applications. Permabond® 268 provides faster set times and improved gap-filling capability compared to conventional cyano..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, handling time
Permabond 268 Cyanoacrylate, General purpose PERMABOND® 268 is a medium-high viscosity cyanoacrylate for large gap fill applications. Permabond® 268 provides faster set times and improved gap-filling capability compared to conventional cyano..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, handling time
Permabond 735 Cyanoacrylate, toughened PERMABOND® 735 is a toughened cyanoacrylate with very good impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable o..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Phenolic, set time, cured
Permabond 738 Cyanoacrylate, toughened PERMABOND 738 is a toughened cyanoacrylate with improved impact and peel strength when compared to a conventional cyanoacrylate. It bonds rapidly at room temperature and its viscosity is stable over..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, handling time
Permabond 102 Cyanoacrylate, General purpose PERMABOND® 102 is a low viscosity general purpose cyanoacrylate adhesive suitable for bonding close-fitting components. It is fast setting and suitable for use on plastics, rubber and metals. Cyano..
Cure Time	0.117 - 0.167 min	0.00194 - 0.00278 hour	ABS, handling time
Permabond 102 Cyanoacrylate, General purpose PERMABOND® 102 is a low viscosity general purpose cyanoacrylate adhesive suitable for bonding close-fitting components. It is fast setting and suitable for use on plastics, rubber and metals. Cyano..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Steel, set time
Permabond 930 Cyanoacrylate PERMABOND 930 is a low odor, nonfogging, nonfrosting cyanoacrylate. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated. The ..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Steel, set time
Permabond 931 Cyanoacrylate PERMABOND 931 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, set time
Permabond 931 Cyanoacrylate PERMABOND 931 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Steel, set time
Permabond 932 Cyanoacrylate PERMABOND 932 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, set time
Permabond 932 Cyanoacrylate PERMABOND 932 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Steel, set time
Permabond 935 Cyanoacrylate The PERMABOND 930 series is a family of low odor, non-fogging, non-frosting cyanoacrylates. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyano..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	Buna N Rubber, set time
Permabond 935 Cyanoacrylate The PERMABOND 930 series is a family of low odor, non-fogging, non-frosting cyanoacrylates. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyano..
Cure Time	0.100 - 0.167 min	0.00167 - 0.00278 hour	Plastic set time
Lord Adhesives 5019 Fast Setting, High Elasticity, High Viscosity Ethyl Cyanoacrylate Adhesive Lord Cyanoacrylate AdhesivesLordÂ® Cyanoacrylate Adhesives were developed for production situations requiring instant bonds and immediate handling strength, particularly when bonding rubber, metal..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour
Tra-Con Tra-Bond 575T01 Anaerobic Adhesive TRA-BOND 575T01 is a high strength, very fast cure, single component anaerobic retaining adhesive for fiber optic terminations. This product cures when confined in the absence of air between close f..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	UV exposure
Tra-Con Tra-Bond 546S05 Dual-Cure Acrylate TRA-BOND 546S05 is a dual cure (UV/heat) acrylate featuring excellent adhesion to glass. Ultimate Tg attained and shadowed areas cured with 15 minute exposure to 100-120°C.Information provided by T..
Cure Time	0.0333 - 0.167 min	0.000556 - 0.00278 hour	10-20 mil thick layers cured with Dymax 5000-EC at 2 inches. Thicker layers may require more cure time.
Dymax 9001v3.0 Low Modulus Clear Microencapsulant High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9001v3.0 Low Modulus Clear MicroencapsulantLowest stress potting and encapsulation on ceramic, FR-4 or flexible PCBs..
Cure Time	0.0167 - 0.167 min	0.000278 - 0.00278 hour	Time to Handling
3M Scotch-Weld™ MG05 PR Medical Grade Instant Adhesive 3M™ Scotch-Weld™ Medical Grade Instant Adhesive are intended for use on a wide variety of materials used in the construction of disposable medical assemblies. They will quickly bond metals, plasti..
Cure Time	0.0167 - 0.167 min	0.000278 - 0.00278 hour	Time to Handling Strength
3M Scotch-Weld™ PR5 Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates ..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	PVC, handling time
Permabond 943 Cyanoacrylate, low odor PERMABOND 943 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad..
Cure Time	0.0833 - 0.167 min	0.00139 - 0.00278 hour	ABS, handling time
Permabond 943 Cyanoacrylate, low odor PERMABOND 943 is a low odor, non-fogging non-frosting alkoxyethyl cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate ad..