PTS SAN-80HF High Flow SAN Resin

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS SAN-80HF High Flow SAN Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Melt Flow 25 g/10 min

@Load 10.0 kg,
Temperature 220 °C
25 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength, Yield 73.1 MPa
10600 psi
ASTM D638
Elongation at Break 6.0 %
6.0 %
ASTM D638
Flexural Yield Strength 117.2 MPa
17000 psi
ASTM D790
Flexural Modulus 3.32 GPa
482 ksi
ASTM D790
Izod Impact, Notched 0.210 J/cm

@Thickness 3.17 mm
0.393 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
ASTM D648
Vicat Softening Point 107 °C
225 °F
ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 191 - 210 °C
375 - 410 °F
Middle Barrel Temperature 204 - 221 °C
400 - 430 °F
Front Barrel Temperature 216 - 229 °C
420 - 445 °F
Nozzle Temperature 204 - 229 °C
400 - 445 °F
Mold Temperature 48.9 - 79.4 °C
120 - 175 °F
Drying Temperature 71.1 - 79.4 °C
160 - 175 °F
Dry Time 2 - 3 hour
2 - 3 hour
Injection Pressure 68.3 - 137 MPa
9900 - 19800 psi
Screw Speed 40 - 100 rpm
40 - 100 rpm