- PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4
PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4
| Category | Metal , Nonferrous Metal , Aluminum Alloy |
| Manufacturer | PEAK Werkstoff |
| Trade Name | DISPAL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Property data for Heat Treatment Condition T4 (Quenching in water at RT).Information provided by PEAK Werkstoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.622 - 2.898 g/cc | 0.09473 - 0.1047 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | >= 190 | >= 190 | HV30 |
| Tensile Strength at Break | >= 464 MPa @Temperature 20.0 °C |
>= 67300 psi @Temperature 68.0 °F |
|
| Tensile Strength, Yield | >= 355 MPa @Temperature 20.0 °C |
>= 51500 psi @Temperature 68.0 °F |
|
| Elongation at Break | >= 0.60 % @Temperature 20.0 °C |
>= 0.60 % @Temperature 68.0 °F |
|
| Modulus of Elasticity | >= 73.0 GPa @Temperature 300 °C |
>= 10600 ksi @Temperature 572 °F |
Condition T6 |
| >= 81.0 GPa @Temperature 250 °C |
>= 11700 ksi @Temperature 482 °F |
Condition T6 | |
| >= 96.0 GPa @Temperature 20.0 °C |
>= 13900 ksi @Temperature 68.0 °F |
||
| Poissons Ratio | 0.286 @Temperature 20.0 °C |
0.286 @Temperature 68.0 °F |
Condition F |
| 0.289 @Temperature 100 °C |
0.289 @Temperature 212 °F |
Condition F | |
| 0.29 @Temperature 150 °C |
0.29 @Temperature 302 °F |
Condition F | |
| 0.291 @Temperature 200 °C |
0.291 @Temperature 392 °F |
Condition F | |
| 0.294 @Temperature 300 °C |
0.294 @Temperature 572 °F |
Condition F | |
| 0.294 @Temperature 250 °C |
0.294 @Temperature 482 °F |
Condition F | |
| Fatigue Strength | 206.5 MPa @Temperature 20.0 °C |
29950 psi @Temperature 68.0 °F |
P50% rotary bending values for 5X10<sup>7</sup> cycles |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.3 - 16.3 µm/m-°C @Temperature 20.0 - 100 °C |
8.50 - 9.06 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 16.1 - 17.1 µm/m-°C @Temperature 20.0 - 200 °C |
8.94 - 9.50 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 17.0 - 18.0 µm/m-°C @Temperature 20.0 - 300 °C |
9.44 - 10.0 µin/in-°F @Temperature 68.0 - 572 °F |
||
| Specific Heat Capacity | 0.840 - 0.880 J/g-°C | 0.201 - 0.210 BTU/lb-°F | |
| Thermal Conductivity | 95.30 W/m-K @Temperature 400 °C |
661.4 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| 99.20 W/m-K @Temperature 300 °C |
688.4 BTU-in/hr-ft²-°F @Temperature 572 °F |
||
| 99.20 W/m-K @Temperature 200 °C |
688.4 BTU-in/hr-ft²-°F @Temperature 392 °F |
||
| 99.60 W/m-K @Temperature 100 °C |
691.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| 101.2 W/m-K @Temperature 30.0 °C |
702.3 BTU-in/hr-ft²-°F @Temperature 86.0 °F |
||
| Melting Point | 528 - 784 °C | 982 - 1440 °F | |
| Solidus | 528.1 - 534.1 °C | 982.6 - 993.4 °F | |
| Liquidus | 784.2 - 790.2 °C | 1444 - 1454 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 63 % | 63 % | As Balance |
| Cobalt, Co | 1.0 % | 1.0 % | |
| Copper, Cu | 3.0 % | 3.0 % | |
| Iron, Fe | 3.0 % | 3.0 % | |
| Magnesium, Mg | 1.0 % | 1.0 % | |
| Nickel, Ni | 3.0 % | 3.0 % | |
| Silicon, Si | 25 % | 25 % | |
| Titanium, Ti | 1.0 % | 1.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000910 - 0.0000100 ohm-cm | 0.00000910 - 0.0000100 ohm-cm |