- HOME
- POLYMER SEARCH
- Polymer Property : CTE, linear = 16.1 µm/m-°C
Polymer Property : CTE, linear = 16.1 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.1 - 17.1 µm/m-°C @Temperature 20.0 - 200 °C |
8.94 - 9.50 µin/in-°F @Temperature 68.0 - 392 °F |
|
| PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T6 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 500 °C |
8.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 500 °C |
8.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 20.0 - 800 °C |
8.94 µin/in-°F @Temperature 68.0 - 1470 °F |
|
| Haynes 625SQ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200°F (649Â.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 25.0 - 1000 °C |
8.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 16.1 µm/m-°C @Temperature 871 °C |
8.94 µin/in-°F @Temperature 1600 °F |
|
| Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |
|||