Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 355 MPa @Temperature 20.0 °C |
>= 51500 psi @Temperature 68.0 °F |
|
PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
Tensile Strength, Yield | >= 355 MPa | >= 51500 psi | |
MetalTek Nitronic® 33 Austenitic Stainless Steel Produced under license of ARMCO Advanced Materials Corp. Information provided by MetalTekWrought Grade NITRONIC 33® |
|||
Tensile Strength, Yield | 355 MPa | 51500 psi | |
Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Yield | >= 355 MPa | >= 51500 psi | |
SSAB Tunnplat Domex® 355MC HSLA Steel HSLA SteelCharacteristics: For hot-dip galvanizing, a thin Zn coating (50-80 microns) is specified.Domex® MC grade steels conform to the provisions of EN 10149-2 standard and often have better pr.. |
|||
Tensile Strength, Yield | >= 355 MPa | >= 51500 psi | |
ThyssenKrupp COR-TEN A Structural Steel This Material Specification applies to plates up to 12.5 mm in thickness made from COR-TEN A.Definition: Weathering means that due to its chemical composition the COR-TEN A steel, when utilized unpr.. |
|||
Tensile Strength, Yield | >= 355 MPa @Thickness 16.0 mm |
>= 51500 psi @Thickness 0.630 in |
|
ThyssenKrupp XABO® 355 Structural Steel This Material Specification applies to thermomechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | >= 355 MPa | >= 51500 psi | |
ThyssenKrupp PAS 355 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio.. |
|||
Tensile Strength, Yield | >= 355 MPa @Thickness 16.0 mm |
>= 51500 psi @Thickness 0.630 in |
|
ThyssenKrupp XABO® 355 T Structural Steel This Material Specification applies to thermomechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | 355 MPa @Strain 0.200 % |
51500 psi @Strain 0.200 % |
typical |
ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Annealed Allegheny Ludlum Type 420 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles.. |