PCC-Advanced Forming Technology AlSiC-SD Metal Matrix Composite

Category	Metal , Metal Matrix Composite
Manufacturer	PCC-Advanced Forming Technology
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PCC-Advanced Forming Technology AlSiC-SD Metal Matrix Composite.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AlSiC metal matrix composites are formed by pressure infiltrating molten aluminum into silicon carbide preforms. This method of casting is typically used in applications where solution requirements include high strength, lightweight, custom CTE and high thermal conductivity. PCC offers AlSiC with a composition varying between 30% to 74% silicon carbide by volume, depending on the application. This flexible material system allows PCC Composites to produce a part that can be tailored to exact solution requirements.Infomation provided by PCC-Advanced Forming Technology.

Physical Properties	Metric	English	Comments
Density	3.02 g/cc	0.109 lb/in³

Mechanical Properties	Metric	English
Hardness, Rockwell B	88	88
Tensile Strength, Ultimate	249 MPa	36100 psi
Modulus of Elasticity	246 GPa	35700 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	7.30 µm/m-°C @Temperature 20.0 - 30.0 °C	4.06 µin/in-°F @Temperature 68.0 - 86.0 °F	X-Direction
	8.10 µm/m-°C @Temperature 20.0 - 30.0 °C	4.50 µin/in-°F @Temperature 68.0 - 86.0 °F	Y-Direction
Thermal Conductivity	175 W/m-K	1210 BTU-in/hr-ft²-°F
Melting Point	557 - 613 °C	1030 - 1140 °F
Solidus	557 °C	1030 °F
Liquidus	613 °C	1140 °F