NOVA Chemicals Novapol® PF-0218-F Butene LLDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | NOVA Chemicals |
| Trade Name | Novapol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® PF-0218-F Butene LLDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Toughness and strength, Ease of extrusionApplications: Cast films, BlendingAdditives: Process stabilizerFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | at 1%; ASTM D882 |
| Impact | 60 | 60 | J/mm; NOVA Chemicals Puncture test |
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.6 g/micron | 269 g/mil | ASTM D1922 |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F<sub>50</sub>, ASTM D1709/A |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 50 % | 50 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 205 °C | 383 - 401 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blow Up Ratio | 2:1 to 3:1 |