Multibase C6-550 Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-550 Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
Relative, no post cure; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 52
52
no post cure; ASTM D2240
54
54
post cured-2 hours at 177°C; ASTM D2240
54
54
post cured-4 hours at 177°C; ASTM D2240
55
55
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 9.039 MPa
1311 psi
post cured- 4 hours at 177°C; ASTM D412
9.115 MPa
1322 psi
post cured- 8 hours at 177°C; ASTM D412
9.232 MPa
1339 psi
post cured- 2 hours at 177°C; ASTM D412
10.47 MPa
1518 psi
no post cure; ASTM D412
Tensile Strength, Yield 3.20 MPa
464 psi
at 200%, no post cure- press cured for 5 minutes; ASTM D412
3.92 MPa
569 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.92 MPa
569 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
4.12 MPa
598 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 508 %
508 %
post cured- 8 hours at 177°C; ASTM D412
522 %
522 %
post cured- 4 hours at 177°C; ASTM D412
530 %
530 %
post cured- 2 hours at 177°C; ASTM D412
661 %
661 %
no post cure; ASTM D412
Tear Strength 44.7 kN/m
255 pli
Die B, no post cure; ASTM D624
48.2 kN/m
275 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
49.1 kN/m
280 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
50.0 kN/m
285 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
Compression Set 27 %
27 %
no post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 2.0 %
2.0 %
no post cure