Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tear Strength = 48.2 kN/m Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tear Strength 48.2 kN/m
275 pli
ASTM D624
Multibase Multi-Flex® TPE A 8615 BLK
This material is currently used in caster wheels where higher abrasion resistance is required. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tear Strength >= 48.2 kN/m
>= 275 pli
ASTM D624
Multibase Multi-Flex® TPE G 7680 BLK
The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tear Strength 48.2 kN/m
275 pli
Die C, 510 mm/min; ASTM D624
PolyOne Geon™ Vinyl Flexible B80MB Polyvinyl Chloride, Flexible (PVC, Flexible)
Information provided by PolyOne
Tear Strength 48.2 kN/m
275 pli
Graves
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 66A
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tear Strength 48.2 kN/m
275 pli
ASTM D624
ITW Devcon Flexane® Rubber Repair / Castable Urethane Fast Cure, Black
Information provided by ITW Devcon
Tear Strength 48.2 kN/m
275 pli
Initial Tear Strength
Saint-Gobain CHR® SG33-06(R) Industrial Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab..
Tear Strength 48.2 kN/m
275 pli
Initial Tear Strength
Saint-Gobain CHR® SG35-06(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab..
Tear Strength 48.2 kN/m
275 pli
Initial Tear Strength
Saint-Gobain CHR® SG35-10(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab..
Tear Strength 48.2 kN/m
275 pli
Initial Tear Strength
Saint-Gobain CHR® SG36-06(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab..
Tear Strength 48.2 kN/m
275 pli
Initial Tear Strength
Saint-Gobain CHR® SG36-10(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
Description: PTFE glass provide dimensional stability, high tensile strength and edge tear, operates over a temperature range from -100°F to +500°F (-73°C to 260°C), and offers better ab..
Tear Strength 48.2 kN/m
275 pli
Fill/Transverse direction
Saint-Gobain COHRlastic® 3016 Low Temperature Flexibility Silicone Coated Fabric
Description: Saint Gobain Performance Plastics CHR standard COHRlastic silicone coated fabrics, available from stock, have silicone rubber dispersion coated on both sides of fiberglass. They are thi..
Tear Strength 48.2 kN/m
275 pli
Graves
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 66A
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tear Strength 48.2 kN/m
275 pli
Dow Corning SILASTIC® LSR 9682-50 PARTS A&B
50 Durometer, 2-part, 1 to 1 mix, clear Liquid Silicone RubberInformation provided by Dow Corning
Tear Strength 48.2 kN/m
275 pli
Cytec EN-9 (Conap) Casting, Potting, and Molding Compound
High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable..
Tear Strength 48.2 kN/m
275 pli
Cytec EN-9 (OZR) (Conap) Casting, Potting, and Molding Compound
High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable..
Tear Strength 48.2 kN/m
275 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
Multibase C6-550 Dow-Corning Class VI Elastomer
Information provided by Multibase
Copyright © lookpolymers.com All Rights Reserved