Master Bond EP45HT-1 Adhesive Resists Exposure to Sterilization
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Master Bond Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Master Bond EP45HT-1 Adhesive Resists Exposure to Sterilization.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Master Bond Polymer System EP45HT-1 is a remarkably fast curing, medium viscosity, two component epoxy compound formulated for high performance casting and bonding. It is 100% reactive and does not contain any diluents, solvents or other volatiles. Master Bond Polymer System EP45HT-1 is readily prepared for use by mixing the two components with a convenient two (2) to one (1) ratio by weight. Cure is moderately fast even at relatively low temperatures and high relative humidities. The ready cure characteristics coupled with excellent thermal stability, resistance to blushing and exudation, high toughness and superior wear resistance make EP45HT-1 particularly attractive for applications where new castings must be put into service within a matter of hours and then perform well over long periods of service especially where long term retention of dimensional stability is important. Recommended cure is to heat for approximately 2 hours at 160-180°F for gelation and then increasing the temperature to around 300°F and heating for 3-4 hours to complete cure. Master Bond Polymer System EP45HT-1 has proven ideally suited for industrial as well as institutional and commercial casting applications particularly in applications requiring durability, chemical resistance, easy, low cost maintenance and high degree of dimensional stability. It is highly recommended for casting and bonding in the electronic, electrical, electro-mechanical, computer, optical and related industries.Product Advantages: Convenient mixing: easy-to-use mix ratio, two (2) to one (1) by weight. 100% reactive: minimum shrinkage upon cure. Fast cures with convenient tack-free time even at moderate temperatures and high relative humidity. Resistance to blushing and exudation. Superior thermal stability up to 400-450°F service . High toughness and long term dimensional stability. Excellent long term dimensional stability. High bonding strength to substrates. Safety hardener with minimum irritation and skin sensitizing effects compared to conventionalInformation provided by MasterBond®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | <= 0.50 % | <= 0.50 % | 48 hrs immersion |
| Viscosity | 800 - 1000 cP | 800 - 1000 cP | Part A |
| 3000 - 5000 cP | 3000 - 5000 cP | Part B |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.1 MPa @Temperature 177 °C |
4510 psi @Temperature 350 °F |
|
| 56.8 MPa @Temperature 121 °C |
8240 psi @Temperature 250 °F |
||
| 64.8 MPa @Temperature 65.6 °C |
9400 psi @Temperature 150 °F |
||
| 76.5 MPa @Temperature 25.0 °C |
11100 psi @Temperature 77.0 °F |
||
| Elongation at Break | 0.61 % @Temperature 25.0 °C |
0.61 % @Temperature 77.0 °F |
|
| 0.73 % @Temperature 65.6 °C |
0.73 % @Temperature 150 °F |
||
| 1.105 % @Temperature 121 °C |
1.105 % @Temperature 250 °F |
||
| 1.78 % @Temperature 177 °C |
1.78 % @Temperature 350 °F |
||
| Tensile Modulus | 4.41 GPa @Temperature 177 °C |
640 ksi @Temperature 350 °F |
|
| 6.41 GPa @Temperature 121 °C |
930 ksi @Temperature 250 °F |
||
| 9.65 GPa @Temperature 65.6 °C |
1400 ksi @Temperature 150 °F |
||
| 14.2 GPa @Temperature 25.0 °C |
2060 ksi @Temperature 77.0 °F |
||
| Flexural Strength | 41.4 MPa @Temperature 177 °C |
6000 psi @Temperature 350 °F |
|
| 75.57 MPa @Temperature 121 °C |
10960 psi @Temperature 250 °F |
||
| 88.3 MPa @Temperature 65.6 °C |
12800 psi @Temperature 150 °F |
||
| 106 MPa @Temperature 25.0 °C |
15400 psi @Temperature 77.0 °F |
||
| Flexural Modulus | 3.93 GPa @Temperature 177 °C |
570 ksi @Temperature 350 °F |
|
| 6.34 GPa @Temperature 121 °C |
920 ksi @Temperature 250 °F |
||
| 8.07 GPa @Temperature 65.6 °C |
1170 ksi @Temperature 150 °F |
||
| 13.2 GPa @Temperature 25.0 °C |
1910 ksi @Temperature 77.0 °F |
||
| Taber Abrasion, mg/1000 Cycles | <= 24 @Load 2.00 kg |
<= 24 @Load 4.41 lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.1 µm/m-°C | 20.1 µin/in-°F | |
| Heat Distortion Temperature | 42.2 °C | 108 °F | |
| Flash Point | 90.6 °C | 195 °F | |
| 96.7 °C | 206 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gardner Color Number | <= 2.0 | <= 2.0 | |
| <= 3.0 | <= 3.0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 180 - 240 min @Temperature 149 °C |
3.00 - 4.00 hour @Temperature 300 °F |
|
| Pot Life | >= 180 min | >= 180 min | 400 gram batch |
| Gel Time | 120 min @Temperature 71.1 - 82.2 °C |
120 min @Temperature 160 - 180 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mixing Ratio (A to B) | 2/1 | by weight |