LG Chemical LUCON CP2100-KA02 PC+CF

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced
Manufacturer LG Chemical
Trade Name LUCON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUCON CP2100-KA02 PC+CF.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description Injection Molding Grade, PC+CF, Electrostatic Dissipation, Low Surface ResistanceApplication: LCD Tray, HDD BracketCAS No. 103598-77-2 and 7440-44-0Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0030 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0030 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 108 MPa

@Thickness 3.20 mm
 15600 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 3.0 %

@Thickness 3.20 mm
 >= 3.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 147 MPa

@Thickness 6.40 mm
 21300 psi

@Thickness 0.252 in
 15mm/min; ASTM D790
Flexural Modulus 6.67 GPa

@Thickness 6.40 mm
 967 ksi

@Thickness 0.252 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.10 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 139 °C

@Thickness 6.40 mm
 282 °F

@Thickness 0.252 in
 ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
Flammability, UL94 V-1

@Thickness >=3.00 mm
 V-1

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Surface Resistance 10000 - 1.00e+9 ohm
10000 - 1.00e+9 ohm
IEC 60093
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 290 °C
536 - 554 °F
Injection Molding
Middle Barrel Temperature 290 - 300 °C
554 - 572 °F
Injection Molding
Front Barrel Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Injection Molding
Melt Temperature 290 - 310 °C
554 - 590 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 5.00 - 7.00 hour
5.00 - 7.00 hour
Injection Molding
Back Pressure <= 1.96 MPa
<= 284 psi
Injection Molding
Screw Speed <= 100 rpm
<= 100 rpm
Injection Molding