LATI Latilub 66-02S PA66, Silicone Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 66-02S PA66, Silicone Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyamide 66 (PA66). Silicone. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.13 g/cc	0.0408 lb/inÂ³
Linear Mold Shrinkage, Flow	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in
Linear Mold Shrinkage, Transverse	0.0125 - 0.0155 cm/cm	0.0125 - 0.0155 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	70.0 MPa	10200 psi
Elongation at Break	30 %	30 %
Elongation at Yield	5.0 %	5.0 %
Tensile Modulus	3.00 GPa	435 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	0.900 J/cmÂ²	4.28 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.25	0.25
Coefficient of Friction, Static	0.27	0.27
K (wear) Factor	44.0 x 10^-8 mmÂ³/N-M	21.8 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	215 Â°C	419 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	65.0 Â°C	149 Â°F
Vicat Softening Point	240 Â°C @Load 5.00 kg	464 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	260 - 290 Â°C	500 - 554 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa